Investigation of arc stability, microstructure evolution and corrosion resistance in underwater wet FCAW of duplex stainless steel

Underwater wet flux-cored arc welding (FCAW) process was used to join 2205 duplex stainless steel using Ni-based filler under three different heat inputs of 16.9 kJ/cm, 23.5 kJ/cm and 32 kJ/cm. The arc stability, microstructure and corrosion resistance with different heat inputs were studied. The re...

Descripción completa

Guardado en:

Detalles Bibliográficos
Autores principales:	Qiang Ma, Chuncheng Luo, Shixiong Liu, Hongliang Li, Pengfei Wang, Duo Liu, Yucheng Lei
Formato:	article
Lenguaje:	EN
Publicado:	Elsevier 2021
Materias:	Arc stability Welding quality 2205 duplex stainless steels Underwater wet welding FCAW Mining engineering. Metallurgy TN1-997
Acceso en línea:	https://doaj.org/article/b708a2a565284aa58f78d30d23090955
Etiquetas:	Agregar Etiqueta Sin Etiquetas, Sea el primero en etiquetar este registro!

id	oai:doaj.org-article:b708a2a565284aa58f78d30d23090955
record_format	dspace
spelling	oai:doaj.org-article:b708a2a565284aa58f78d30d230909552021-11-20T05:06:39ZInvestigation of arc stability, microstructure evolution and corrosion resistance in underwater wet FCAW of duplex stainless steel2238-785410.1016/j.jmrt.2021.11.023https://doaj.org/article/b708a2a565284aa58f78d30d230909552021-11-01T00:00:00Zhttp://www.sciencedirect.com/science/article/pii/S2238785421013016https://doaj.org/toc/2238-7854Underwater wet flux-cored arc welding (FCAW) process was used to join 2205 duplex stainless steel using Ni-based filler under three different heat inputs of 16.9 kJ/cm, 23.5 kJ/cm and 32 kJ/cm. The arc stability, microstructure and corrosion resistance with different heat inputs were studied. The results showed that the welding process at the heat input of 23.5 kJ/cm was stable with less spatter and good weld appearance. The weld width, weld penetration and dilution ratio increased with increasing heat input. A single-phase austenitic microstructure was obtained for all welds with varied parameters. The heat-affected zone consisted of coarse ferrite and austenite in grain boundary. The grain size of weld zone and heat-affected zone coarsened as the heat input rose. Compared with the base 2205 base metal, the hardness of HAZ increased about 15% while the weld metal changed little. Electrochemical test in 3.5% NaCl solution indicated that the corrosion resistance of the weld metal under high heat input was better, but its corrosion resistance was inferior to that of base materials. Weld metal obtained at 23.5 kJ/cm possessed comprehensive properties in terms of arc stability and corrosion resistance. These results are helpful to promote the application of duplex stainless steel in the fields of nuclear power fields.Qiang MaChuncheng LuoShixiong LiuHongliang LiPengfei WangDuo LiuYucheng LeiElsevierarticleArc stabilityWelding quality2205 duplex stainless steelsUnderwater wet weldingFCAWMining engineering. MetallurgyTN1-997ENJournal of Materials Research and Technology, Vol 15, Iss , Pp 5482-5495 (2021)
institution	DOAJ
collection	DOAJ
language	EN
topic	Arc stability Welding quality 2205 duplex stainless steels Underwater wet welding FCAW Mining engineering. Metallurgy TN1-997
spellingShingle	Arc stability Welding quality 2205 duplex stainless steels Underwater wet welding FCAW Mining engineering. Metallurgy TN1-997 Qiang Ma Chuncheng Luo Shixiong Liu Hongliang Li Pengfei Wang Duo Liu Yucheng Lei Investigation of arc stability, microstructure evolution and corrosion resistance in underwater wet FCAW of duplex stainless steel
description	Underwater wet flux-cored arc welding (FCAW) process was used to join 2205 duplex stainless steel using Ni-based filler under three different heat inputs of 16.9 kJ/cm, 23.5 kJ/cm and 32 kJ/cm. The arc stability, microstructure and corrosion resistance with different heat inputs were studied. The results showed that the welding process at the heat input of 23.5 kJ/cm was stable with less spatter and good weld appearance. The weld width, weld penetration and dilution ratio increased with increasing heat input. A single-phase austenitic microstructure was obtained for all welds with varied parameters. The heat-affected zone consisted of coarse ferrite and austenite in grain boundary. The grain size of weld zone and heat-affected zone coarsened as the heat input rose. Compared with the base 2205 base metal, the hardness of HAZ increased about 15% while the weld metal changed little. Electrochemical test in 3.5% NaCl solution indicated that the corrosion resistance of the weld metal under high heat input was better, but its corrosion resistance was inferior to that of base materials. Weld metal obtained at 23.5 kJ/cm possessed comprehensive properties in terms of arc stability and corrosion resistance. These results are helpful to promote the application of duplex stainless steel in the fields of nuclear power fields.
format	article
author	Qiang Ma Chuncheng Luo Shixiong Liu Hongliang Li Pengfei Wang Duo Liu Yucheng Lei
author_facet	Qiang Ma Chuncheng Luo Shixiong Liu Hongliang Li Pengfei Wang Duo Liu Yucheng Lei
author_sort	Qiang Ma
title	Investigation of arc stability, microstructure evolution and corrosion resistance in underwater wet FCAW of duplex stainless steel
title_short	Investigation of arc stability, microstructure evolution and corrosion resistance in underwater wet FCAW of duplex stainless steel
title_full	Investigation of arc stability, microstructure evolution and corrosion resistance in underwater wet FCAW of duplex stainless steel
title_fullStr	Investigation of arc stability, microstructure evolution and corrosion resistance in underwater wet FCAW of duplex stainless steel
title_full_unstemmed	Investigation of arc stability, microstructure evolution and corrosion resistance in underwater wet FCAW of duplex stainless steel
title_sort	investigation of arc stability, microstructure evolution and corrosion resistance in underwater wet fcaw of duplex stainless steel
publisher	Elsevier
publishDate	2021
url	https://doaj.org/article/b708a2a565284aa58f78d30d23090955
work_keys_str_mv	AT qiangma investigationofarcstabilitymicrostructureevolutionandcorrosionresistanceinunderwaterwetfcawofduplexstainlesssteel AT chunchengluo investigationofarcstabilitymicrostructureevolutionandcorrosionresistanceinunderwaterwetfcawofduplexstainlesssteel AT shixiongliu investigationofarcstabilitymicrostructureevolutionandcorrosionresistanceinunderwaterwetfcawofduplexstainlesssteel AT hongliangli investigationofarcstabilitymicrostructureevolutionandcorrosionresistanceinunderwaterwetfcawofduplexstainlesssteel AT pengfeiwang investigationofarcstabilitymicrostructureevolutionandcorrosionresistanceinunderwaterwetfcawofduplexstainlesssteel AT duoliu investigationofarcstabilitymicrostructureevolutionandcorrosionresistanceinunderwaterwetfcawofduplexstainlesssteel AT yuchenglei investigationofarcstabilitymicrostructureevolutionandcorrosionresistanceinunderwaterwetfcawofduplexstainlesssteel
_version_	1718419619134308352

Investigation of arc stability, microstructure evolution and corrosion resistance in underwater wet FCAW of duplex stainless steel

Ejemplares similares