Analysis of Wear-Resisting Properties of a Sintered Sample Obtained from Steel X13 Machined Using EDM
The article presents the results of a study of the wear resistance of sintered specimens from electroerosive powder of steel X13, obtained in butyl alcohol. The friction coefficient was 0.950, the width of the wear groove was 455.9 µm, the depth of the wear groove was 6 µm, the wear factor of the sa...
Enregistré dans:
| Auteurs principaux: | , , , |
|---|---|
| Format: | article |
| Langue: | EN FR |
| Publié: |
EDP Sciences
2021
|
| Sujets: | |
| Accès en ligne: | https://doaj.org/article/b748b3edcee44a469acd68b72cbaafa6 |
| Tags: |
Ajouter un tag
Pas de tags, Soyez le premier à ajouter un tag!
|
| Résumé: | The article presents the results of a study of the wear resistance of sintered specimens from electroerosive powder of steel X13, obtained in butyl alcohol. The friction coefficient was 0.950, the width of the wear groove was 455.9 µm, the depth of the wear groove was 6 µm, the wear factor of the sample was 1.676x10-6 mm3 N-1m-1. |
|---|