Analysis of Wear-Resisting Properties of a Sintered Sample Obtained from Steel X13 Machined Using EDM
The article presents the results of a study of the wear resistance of sintered specimens from electroerosive powder of steel X13, obtained in butyl alcohol. The friction coefficient was 0.950, the width of the wear groove was 455.9 µm, the depth of the wear groove was 6 µm, the wear factor of the sa...
Guardado en:
| Autores principales: | , , , |
|---|---|
| Formato: | article |
| Lenguaje: | EN FR |
| Publicado: |
EDP Sciences
2021
|
| Materias: | |
| Acceso en línea: | https://doaj.org/article/b748b3edcee44a469acd68b72cbaafa6 |
| Etiquetas: |
Agregar Etiqueta
Sin Etiquetas, Sea el primero en etiquetar este registro!
|
| id |
oai:doaj.org-article:b748b3edcee44a469acd68b72cbaafa6 |
|---|---|
| record_format |
dspace |
| spelling |
oai:doaj.org-article:b748b3edcee44a469acd68b72cbaafa62021-11-08T15:20:43ZAnalysis of Wear-Resisting Properties of a Sintered Sample Obtained from Steel X13 Machined Using EDM2261-236X10.1051/matecconf/202134602018https://doaj.org/article/b748b3edcee44a469acd68b72cbaafa62021-01-01T00:00:00Zhttps://www.matec-conferences.org/articles/matecconf/pdf/2021/15/matecconf_icmtmte2021_02018.pdfhttps://doaj.org/toc/2261-236XThe article presents the results of a study of the wear resistance of sintered specimens from electroerosive powder of steel X13, obtained in butyl alcohol. The friction coefficient was 0.950, the width of the wear groove was 455.9 µm, the depth of the wear groove was 6 µm, the wear factor of the sample was 1.676x10-6 mm3 N-1m-1.Ageev E.V.Khardikov S.V.Loktionova O.G.Kolmykov V.I.EDP SciencesarticleEngineering (General). Civil engineering (General)TA1-2040ENFRMATEC Web of Conferences, Vol 346, p 02018 (2021) |
| institution |
DOAJ |
| collection |
DOAJ |
| language |
EN FR |
| topic |
Engineering (General). Civil engineering (General) TA1-2040 |
| spellingShingle |
Engineering (General). Civil engineering (General) TA1-2040 Ageev E.V. Khardikov S.V. Loktionova O.G. Kolmykov V.I. Analysis of Wear-Resisting Properties of a Sintered Sample Obtained from Steel X13 Machined Using EDM |
| description |
The article presents the results of a study of the wear resistance of sintered specimens from electroerosive powder of steel X13, obtained in butyl alcohol. The friction coefficient was 0.950, the width of the wear groove was 455.9 µm, the depth of the wear groove was 6 µm, the wear factor of the sample was 1.676x10-6 mm3 N-1m-1. |
| format |
article |
| author |
Ageev E.V. Khardikov S.V. Loktionova O.G. Kolmykov V.I. |
| author_facet |
Ageev E.V. Khardikov S.V. Loktionova O.G. Kolmykov V.I. |
| author_sort |
Ageev E.V. |
| title |
Analysis of Wear-Resisting Properties of a Sintered Sample Obtained from Steel X13 Machined Using EDM |
| title_short |
Analysis of Wear-Resisting Properties of a Sintered Sample Obtained from Steel X13 Machined Using EDM |
| title_full |
Analysis of Wear-Resisting Properties of a Sintered Sample Obtained from Steel X13 Machined Using EDM |
| title_fullStr |
Analysis of Wear-Resisting Properties of a Sintered Sample Obtained from Steel X13 Machined Using EDM |
| title_full_unstemmed |
Analysis of Wear-Resisting Properties of a Sintered Sample Obtained from Steel X13 Machined Using EDM |
| title_sort |
analysis of wear-resisting properties of a sintered sample obtained from steel x13 machined using edm |
| publisher |
EDP Sciences |
| publishDate |
2021 |
| url |
https://doaj.org/article/b748b3edcee44a469acd68b72cbaafa6 |
| work_keys_str_mv |
AT ageevev analysisofwearresistingpropertiesofasinteredsampleobtainedfromsteelx13machinedusingedm AT khardikovsv analysisofwearresistingpropertiesofasinteredsampleobtainedfromsteelx13machinedusingedm AT loktionovaog analysisofwearresistingpropertiesofasinteredsampleobtainedfromsteelx13machinedusingedm AT kolmykovvi analysisofwearresistingpropertiesofasinteredsampleobtainedfromsteelx13machinedusingedm |
| _version_ |
1718441786785923072 |