Corrosion inhibition of mild steel in sulfuric acid solution by loquat (Eriobotrya japonica Lindl.) leaves extract
Abstract The inhibition performance and mechanism of loquat leaves extract (LLE) for the corrosion of mild steel in 0.5 M H2SO4 were investigated using weight loss method, electrochemical measurements and scanning electron microscope (SEM). The results revealed that LLE acted as a modest cathodic in...
Guardado en:
| Autores principales: | , , , |
|---|---|
| Formato: | article |
| Lenguaje: | EN |
| Publicado: |
Nature Portfolio
2018
|
| Materias: | |
| Acceso en línea: | https://doaj.org/article/bc976435b88749c8a2bb74a3cd654c13 |
| Etiquetas: |
Agregar Etiqueta
Sin Etiquetas, Sea el primero en etiquetar este registro!
|
| Sumario: | Abstract The inhibition performance and mechanism of loquat leaves extract (LLE) for the corrosion of mild steel in 0.5 M H2SO4 were investigated using weight loss method, electrochemical measurements and scanning electron microscope (SEM). The results revealed that LLE acted as a modest cathodic inhibitor, its inhibition efficiency increased with the concentration of LLE and reached a maximum value of 96% at the 100% V/V concentration, but decreased with incremental temperature. Besides, it was found that the adsorption of LLE on steel surface obeyed Langmuir adsorption isotherm, and then the thermodynamic and kinetic parameters were further determined accordingly. Furthermore, LLE was preliminarily separated by pH-gradient sedimentation and the synergistic inhibition between the isolates was investigated. |
|---|