NaCl and Na2SO4 solution effect on weathering steel visual appearance when the ambient temperature changes cyclically

Visual appearance—colour and texture variation—of weathering steel was compared by testing weathering steel samples in aggressive and non-aggressive conditions, and cyclical changes of ambient temperature. This paper introduces a new method for determining visual appearance of weather-resistant stee...

Descripción completa

Guardado en:
Detalles Bibliográficos
Autores principales: Mindaugas Daukšys, Evelina Bitautaitė, Jūratė Mockienė, Dalia Nizevičienė
Formato: article
Lenguaje:EN
Publicado: Taylor & Francis Group 2019
Materias:
Acceso en línea:https://doaj.org/article/bced34613d6942bb89bf92d78e804e8a
Etiquetas: Agregar Etiqueta
Sin Etiquetas, Sea el primero en etiquetar este registro!
id oai:doaj.org-article:bced34613d6942bb89bf92d78e804e8a
record_format dspace
spelling oai:doaj.org-article:bced34613d6942bb89bf92d78e804e8a2021-11-04T15:51:56ZNaCl and Na2SO4 solution effect on weathering steel visual appearance when the ambient temperature changes cyclically2331-191610.1080/23311916.2019.1659124https://doaj.org/article/bced34613d6942bb89bf92d78e804e8a2019-01-01T00:00:00Zhttp://dx.doi.org/10.1080/23311916.2019.1659124https://doaj.org/toc/2331-1916Visual appearance—colour and texture variation—of weathering steel was compared by testing weathering steel samples in aggressive and non-aggressive conditions, and cyclical changes of ambient temperature. This paper introduces a new method for determining visual appearance of weather-resistant steel in different environmental conditions. Weathering steel samples were tested in H2O, 3% NaCl and 3% Na2SO4 solutions under ambient temperature changing from +20°C to −20°C per day. The structure of steel surface viewed under optical microscope revealed corrosion products in all steel samples. X-ray diffraction analysis of corrosion products revealed the presence of oxy-hydroxides, such as lepidocrocite (ɣ-FeO(OH)), goethite (α-FeO(OH)) and magnetite (Fe3O4) in different environment. Optical microscopy images of corroded surfaces had different visual appearance and orange, yellow, sandy, black or anthracite colours, which indicate that the corrosion products primarily contain lepidocrocite (ɣ-FeO(OH)), goethite (α-FeO(OH)) and magnetite (Fe3O4). EDS analysis revealed that the rust of samples kept in 3% NaCl solution had the highest amount of iron ions.Mindaugas DaukšysEvelina BitautaitėJūratė MockienėDalia NizevičienėTaylor & Francis Grouparticleweathering steelnacl and na2so4 solutionvisual appearancexrd analysiseds analysisEngineering (General). Civil engineering (General)TA1-2040ENCogent Engineering, Vol 6, Iss 1 (2019)
institution DOAJ
collection DOAJ
language EN
topic weathering steel
nacl and na2so4 solution
visual appearance
xrd analysis
eds analysis
Engineering (General). Civil engineering (General)
TA1-2040
spellingShingle weathering steel
nacl and na2so4 solution
visual appearance
xrd analysis
eds analysis
Engineering (General). Civil engineering (General)
TA1-2040
Mindaugas Daukšys
Evelina Bitautaitė
Jūratė Mockienė
Dalia Nizevičienė
NaCl and Na2SO4 solution effect on weathering steel visual appearance when the ambient temperature changes cyclically
description Visual appearance—colour and texture variation—of weathering steel was compared by testing weathering steel samples in aggressive and non-aggressive conditions, and cyclical changes of ambient temperature. This paper introduces a new method for determining visual appearance of weather-resistant steel in different environmental conditions. Weathering steel samples were tested in H2O, 3% NaCl and 3% Na2SO4 solutions under ambient temperature changing from +20°C to −20°C per day. The structure of steel surface viewed under optical microscope revealed corrosion products in all steel samples. X-ray diffraction analysis of corrosion products revealed the presence of oxy-hydroxides, such as lepidocrocite (ɣ-FeO(OH)), goethite (α-FeO(OH)) and magnetite (Fe3O4) in different environment. Optical microscopy images of corroded surfaces had different visual appearance and orange, yellow, sandy, black or anthracite colours, which indicate that the corrosion products primarily contain lepidocrocite (ɣ-FeO(OH)), goethite (α-FeO(OH)) and magnetite (Fe3O4). EDS analysis revealed that the rust of samples kept in 3% NaCl solution had the highest amount of iron ions.
format article
author Mindaugas Daukšys
Evelina Bitautaitė
Jūratė Mockienė
Dalia Nizevičienė
author_facet Mindaugas Daukšys
Evelina Bitautaitė
Jūratė Mockienė
Dalia Nizevičienė
author_sort Mindaugas Daukšys
title NaCl and Na2SO4 solution effect on weathering steel visual appearance when the ambient temperature changes cyclically
title_short NaCl and Na2SO4 solution effect on weathering steel visual appearance when the ambient temperature changes cyclically
title_full NaCl and Na2SO4 solution effect on weathering steel visual appearance when the ambient temperature changes cyclically
title_fullStr NaCl and Na2SO4 solution effect on weathering steel visual appearance when the ambient temperature changes cyclically
title_full_unstemmed NaCl and Na2SO4 solution effect on weathering steel visual appearance when the ambient temperature changes cyclically
title_sort nacl and na2so4 solution effect on weathering steel visual appearance when the ambient temperature changes cyclically
publisher Taylor & Francis Group
publishDate 2019
url https://doaj.org/article/bced34613d6942bb89bf92d78e804e8a
work_keys_str_mv AT mindaugasdauksys naclandna2so4solutioneffectonweatheringsteelvisualappearancewhentheambienttemperaturechangescyclically
AT evelinabitautaite naclandna2so4solutioneffectonweatheringsteelvisualappearancewhentheambienttemperaturechangescyclically
AT juratemockiene naclandna2so4solutioneffectonweatheringsteelvisualappearancewhentheambienttemperaturechangescyclically
AT dalianizeviciene naclandna2so4solutioneffectonweatheringsteelvisualappearancewhentheambienttemperaturechangescyclically
_version_ 1718444674938568704