Hierarchical Mesoporous SSZ-13 Chabazite Zeolites for Carbon Dioxide Capture
Artificial carbon dioxide capture is an alternative method to remove the carbon dioxide already accumulated in the atmosphere as well as to stop its release at its large-scale emission points at the source, such as at power plants. However, new adsorbents are needed to make the approach feasible. Fo...
Guardado en:
| Autores principales: | , |
|---|---|
| Formato: | article |
| Lenguaje: | EN |
| Publicado: |
MDPI AG
2021
|
| Materias: | |
| Acceso en línea: | https://doaj.org/article/bd0c56ac539b4e1995d9f1b2d22f1925 |
| Etiquetas: |
Agregar Etiqueta
Sin Etiquetas, Sea el primero en etiquetar este registro!
|
| Sumario: | Artificial carbon dioxide capture is an alternative method to remove the carbon dioxide already accumulated in the atmosphere as well as to stop its release at its large-scale emission points at the source, such as at power plants. However, new adsorbents are needed to make the approach feasible. For this purpose, in this study, hierarchical mesoporous-microporous chabazite-type zeolites were synthesised by applying a dual-templating method. The microporous zeolite structure-directing agent N,N,N-trimethyl-1-adamantanammonium hydroxide was combined with an organosilane mesopore-generating template, 3-(trimethoxysilyl)propyl octadecyl dimethyl ammonium chloride. Materials were characterised for their structural and textural properties and tested for their carbon dioxide capture capacity both in their original sodium form and in their proton-exchanged form by means of breakthrough curve analysis and sorption isotherms. The influence of template ratios on their structure, carbon dioxide capture, and capacity have been identified. All mesoporous materials showed fast adsorption-desorption kinetics due to a reduction in the steric limitations via the introduction of a meso range network of pores. The hierarchical zeolites are recyclable with a negligible loss in crystallinity and carbon dioxide capture capacity, which makes them potential materials for larger-scale application. |
|---|