Fatigue Life Analysis of Aluminum Alloy Notched Specimens under Non-Gaussian Excitation based on Fatigue Damage Spectrum
In this study, a non-Gaussian excitation acceleration method is proposed, using aluminum alloy notched specimens as a research object and measured acceleration signal of a certain airborne bracket, during aircraft flight as input excitations, based on the fatigue damage spectrum (FDS) theory. The ku...
Guardado en:
Autores principales: | Kuanyu Chen, Guangwu Yang, Jianjun Zhang, Shoune Xiao, Yang Xu |
---|---|
Formato: | article |
Lenguaje: | EN |
Publicado: |
Hindawi Limited
2021
|
Materias: | |
Acceso en línea: | https://doaj.org/article/bf0a1adbc3e843c9b56983986fb2f57e |
Etiquetas: |
Agregar Etiqueta
Sin Etiquetas, Sea el primero en etiquetar este registro!
|
Ejemplares similares
-
Fatigue life analysis for 6061-T6 aluminum alloy based on surface roughness.
por: Yali Yang, et al.
Publicado: (2021) -
Effect of specimen thickness on fatigue crack growth behavior of friction stir welded 6063-T5 aluminum alloy
por: Toru TAKASE, et al.
Publicado: (2016) -
Effect of optimal shot peening time on fatigue life for aluminum alloy 6061-T651
por: Ahmed N. Al-Khazraji
Publicado: (2019) -
Analysis of the Effects of Aggressive Shot Peening on Fatigue Life of 7075 T6 Aluminum Alloy
por: Khairallah S. Jabur
Publicado: (2012) -
Analysis of the Effects of Aggressive Shot Peening on Fatigue Life of 7075 – T6 Aluminum Alloy
por: Khairallah S. Jabur
Publicado: (2012)