Properties of high quality paper from rag fibers recycling
In this investigation, soda pulps from old rags applying three pulping times (60, 120 and 180 minutes ) and three levels of active alkali ( 6,8, and 10% NaOH based on OD weight of rag) and pulping temperature of 125º C were produced. Liquor to rag ratio was kept constant at 11:1(based on the weight...
Guardado en:
| Autores principales: | , , |
|---|---|
| Formato: | article |
| Lenguaje: | FA |
| Publicado: |
Regional Information Center for Science and Technology (RICeST)
2012
|
| Materias: | |
| Acceso en línea: | https://doaj.org/article/c19ca1da8d2649cab4f2ee6541420f12 |
| Etiquetas: |
Agregar Etiqueta
Sin Etiquetas, Sea el primero en etiquetar este registro!
|
| Sumario: | In this investigation, soda pulps from old rags applying three pulping times (60, 120 and 180 minutes ) and three levels of active alkali ( 6,8, and 10% NaOH based on OD weight of rag) and pulping temperature of 125º C were produced. Liquor to rag ratio was kept constant at 11:1(based on the weight of the rag). After pulping, hand sheets were made and then both strength and optical properties of hand sheets were measured. It was revealed that, the optimum condition for rag pulping was; 8% active alkali and 120 minutes. At this pulping conditions, the pulping yield and mechanical and optical properties of pulp were measured as yield; 86.46 %, tear index; 20.12 mN.m2/g, burst index; 2.09 kPa.m2/g, breaking length; 1.96 km, brightness; 95.86 % and opacity: 96.39 |
|---|