Hard Chromium Electroplating and Improvement the Properties by the Thermo Chemical Treatments (Solid Carburizing) of Low Carbon Steel

In this research the hard chromium electroplating process, which is one of the common methods of overlay coating was used, by using chromium acid as source of chromium and sulphuric acid as catalyst since the ratio between chromic acid and sulphuric acid is (100 : 1) consequently. Plating process wa...

Descripción completa

Guardado en:

Detalles Bibliográficos
Autores principales:	Ahmed Salloum Abbas, Amin Dway Thamir, Muna Khedier Abbas
Formato:	article
Lenguaje:	EN
Publicado:	Al-Khwarizmi College of Engineering – University of Baghdad 2009
Materias:	Chromium electroplating carbon steel solid carburizing wear Chemical engineering TP155-156 Engineering (General). Civil engineering (General) TA1-2040
Acceso en línea:	https://doaj.org/article/c2ff7c8ebf7b4abeb166d83264d9a294
Etiquetas:	Agregar Etiqueta Sin Etiquetas, Sea el primero en etiquetar este registro!

id	oai:doaj.org-article:c2ff7c8ebf7b4abeb166d83264d9a294
record_format	dspace
spelling	oai:doaj.org-article:c2ff7c8ebf7b4abeb166d83264d9a2942021-12-02T01:10:05ZHard Chromium Electroplating and Improvement the Properties by the Thermo Chemical Treatments (Solid Carburizing) of Low Carbon Steel 1818-1171https://doaj.org/article/c2ff7c8ebf7b4abeb166d83264d9a2942009-01-01T00:00:00Zhttp://www.iasj.net/iasj?func=fulltext&aId=24928https://doaj.org/toc/1818-1171In this research the hard chromium electroplating process, which is one of the common methods of overlay coating was used, by using chromium acid as source of chromium and sulphuric acid as catalyst since the ratio between chromic acid and sulphuric acid is (100 : 1) consequently. Plating process was made by applying current of density (40 Amp / dm2) and the range of solution temperature was (50 55oC) with different time periods (1-5 hr). A low carbon steel type (Ck15) was used as substrate for hard chromium electroplating. Solid carburization was carried out for hard chromium plating specimen at temperature (925oC) with time duration (2 hr) to be followed with quenching and tempering. The phase analysis was conducted by using X ray diffraction. The examination results show that the chromium carbides in plating layer were (Cr23C6, Cr7C3). The microhardness of hard chromium plating specimen was measured, and the results show that the high hardness was about (907HV). After solid carburization the hardness values increase and the results show that the higher hardness for chromium plating layer on low carbon steel surface was (1276 HV). Wear apparatus type (Pin on Disc) was used to study dry sliding wear properties of low carbon steel (As received) and hard chromium plating specimens and solid carburized. The effect of applied normal load on wear rate was studied with weighting method using five normal loads (5, 10, 15, 20, 25 N) at constant sliding speed (2.198 m / sec). The results reveal that the wear rate increases with the increasing of applied normal load. A good improvement in wear resistance was noticed for hard chromium plating specimens as compared with substrate specimen. It was also seen that, the improvement in wear resistance was (94%) as compared with substrate metal when carburizing treatment is carried out on hard chromium plating specimens.Ahmed Salloum AbbasAmin Dway ThamirMuna Khedier AbbasAl-Khwarizmi College of Engineering – University of BaghdadarticleChromium electroplatingcarbon steelsolid carburizingwearChemical engineeringTP155-156Engineering (General). Civil engineering (General)TA1-2040ENAl-Khawarizmi Engineering Journal, Vol 5, Iss 4, Pp 99-114 (2009)
institution	DOAJ
collection	DOAJ
language	EN
topic	Chromium electroplating carbon steel solid carburizing wear Chemical engineering TP155-156 Engineering (General). Civil engineering (General) TA1-2040
spellingShingle	Chromium electroplating carbon steel solid carburizing wear Chemical engineering TP155-156 Engineering (General). Civil engineering (General) TA1-2040 Ahmed Salloum Abbas Amin Dway Thamir Muna Khedier Abbas Hard Chromium Electroplating and Improvement the Properties by the Thermo Chemical Treatments (Solid Carburizing) of Low Carbon Steel
description	In this research the hard chromium electroplating process, which is one of the common methods of overlay coating was used, by using chromium acid as source of chromium and sulphuric acid as catalyst since the ratio between chromic acid and sulphuric acid is (100 : 1) consequently. Plating process was made by applying current of density (40 Amp / dm2) and the range of solution temperature was (50 55oC) with different time periods (1-5 hr). A low carbon steel type (Ck15) was used as substrate for hard chromium electroplating. Solid carburization was carried out for hard chromium plating specimen at temperature (925oC) with time duration (2 hr) to be followed with quenching and tempering. The phase analysis was conducted by using X ray diffraction. The examination results show that the chromium carbides in plating layer were (Cr23C6, Cr7C3). The microhardness of hard chromium plating specimen was measured, and the results show that the high hardness was about (907HV). After solid carburization the hardness values increase and the results show that the higher hardness for chromium plating layer on low carbon steel surface was (1276 HV). Wear apparatus type (Pin on Disc) was used to study dry sliding wear properties of low carbon steel (As received) and hard chromium plating specimens and solid carburized. The effect of applied normal load on wear rate was studied with weighting method using five normal loads (5, 10, 15, 20, 25 N) at constant sliding speed (2.198 m / sec). The results reveal that the wear rate increases with the increasing of applied normal load. A good improvement in wear resistance was noticed for hard chromium plating specimens as compared with substrate specimen. It was also seen that, the improvement in wear resistance was (94%) as compared with substrate metal when carburizing treatment is carried out on hard chromium plating specimens.
format	article
author	Ahmed Salloum Abbas Amin Dway Thamir Muna Khedier Abbas
author_facet	Ahmed Salloum Abbas Amin Dway Thamir Muna Khedier Abbas
author_sort	Ahmed Salloum Abbas
title	Hard Chromium Electroplating and Improvement the Properties by the Thermo Chemical Treatments (Solid Carburizing) of Low Carbon Steel
title_short	Hard Chromium Electroplating and Improvement the Properties by the Thermo Chemical Treatments (Solid Carburizing) of Low Carbon Steel
title_full	Hard Chromium Electroplating and Improvement the Properties by the Thermo Chemical Treatments (Solid Carburizing) of Low Carbon Steel
title_fullStr	Hard Chromium Electroplating and Improvement the Properties by the Thermo Chemical Treatments (Solid Carburizing) of Low Carbon Steel
title_full_unstemmed	Hard Chromium Electroplating and Improvement the Properties by the Thermo Chemical Treatments (Solid Carburizing) of Low Carbon Steel
title_sort	hard chromium electroplating and improvement the properties by the thermo chemical treatments (solid carburizing) of low carbon steel
publisher	Al-Khwarizmi College of Engineering – University of Baghdad
publishDate	2009
url	https://doaj.org/article/c2ff7c8ebf7b4abeb166d83264d9a294
work_keys_str_mv	AT ahmedsalloumabbas hardchromiumelectroplatingandimprovementthepropertiesbythethermochemicaltreatmentssolidcarburizingoflowcarbonsteel AT amindwaythamir hardchromiumelectroplatingandimprovementthepropertiesbythethermochemicaltreatmentssolidcarburizingoflowcarbonsteel AT munakhedierabbas hardchromiumelectroplatingandimprovementthepropertiesbythethermochemicaltreatmentssolidcarburizingoflowcarbonsteel
_version_	1718403282396774400

Hard Chromium Electroplating and Improvement the Properties by the Thermo Chemical Treatments (Solid Carburizing) of Low Carbon Steel

Ejemplares similares