Path-dependent bond-line evolution in equilibrated core honeycomb sandwich structures
During co-cure of honeycomb core sandwich panels, composite facesheets are cured and concurrently bonded to the core, introducing complex interactions that can lead to unsatisfactory bond-line formation. In this work, an in situ co-cure fixture is employed to directly observe the adhesive during pro...
Guardado en:
| Autores principales: | , , , |
|---|---|
| Formato: | article |
| Lenguaje: | EN |
| Publicado: |
Taylor & Francis Group
2020
|
| Materias: | |
| Acceso en línea: | https://doaj.org/article/ca1b798069284f6c8df4e7ec4357ff5f |
| Etiquetas: |
Agregar Etiqueta
Sin Etiquetas, Sea el primero en etiquetar este registro!
|
| Sumario: | During co-cure of honeycomb core sandwich panels, composite facesheets are cured and concurrently bonded to the core, introducing complex interactions that can lead to unsatisfactory bond-line formation. In this work, an in situ co-cure fixture is employed to directly observe the adhesive during processing and identify defect formation mechanisms specific to the bond-line. Relating fillet quality to imposed core pressure reveals the non-linear effect of core pressure. High pressures suppressed voids; intermediate pressures resulted in void growth and entrapment within deformed fillets; and low pressures led to void rupture and small, irregular fillets. Experimental results aided in developing a model to predict void growth in the bond-line. The findings presented here provide insight into the physics controlling the adhesive bond-line evolution during co-cure, which can inform manufacturing decisions to produce higher-quality honeycomb core sandwich structures. |
|---|