The effect of boric acid on the physical and mechanical properties of particleboard made to Urea-formaldehyde resin (UF)
This objective of this investigation was to modify and improve the water resistance of urea formaldehyde (UF) bonded particleboard adding Boric acid to the resin. Four levels (1, 2, 3 and 4) of boric acid based on the dry weight of the bonder were added to the UF resin. Then these mixtures were use...
Guardado en:
| Autores principales: | , , , |
|---|---|
| Formato: | article |
| Lenguaje: | FA |
| Publicado: |
Regional Information Center for Science and Technology (RICeST)
2016
|
| Materias: | |
| Acceso en línea: | https://doaj.org/article/cb0c6185c31042f78c03f611b2758c26 |
| Etiquetas: |
Agregar Etiqueta
Sin Etiquetas, Sea el primero en etiquetar este registro!
|
| Sumario: | This objective of this investigation was to modify and improve the water resistance of urea formaldehyde (UF) bonded particleboard adding Boric acid to the resin. Four levels (1, 2, 3 and 4) of boric acid based on the dry weight of the bonder were added to the UF resin. Then these mixtures were used to produce particleboard. Physical and mechanical properties were examined according to the ASTM, D1013-04. The results showed that the using of this additive increased the water absorption and thickness swelling resistance after 2 and 24 hours immersion in water. Also using this additive increased the internal bonding of the boards after 24 hours after immersion in water, compared to the control sample but in the case of dry samples, the internal bonding decreased compared to the control sample. However it was not lower than standard value. As the Boric acid levels increased to 2 percent, bending strength of the samples was increased compare to the control sample and after this level it was decreased. Also with increasing the levels to 4 percent, modulus of elasticity of boards were increased compare to the control sample |
|---|