Thermotropic liquid crystalline copolyester fibers according to various heat treatment conditions
Abstract Thermotropic liquid crystal copolyester (TLCP) was synthesized using a melt polymerization method, with a molar ratio composition of 2,5-diethoxy terephthalic acid (ETA), hydroquinone (HQ), and p-hydroxybenzoic acid (HBA) of 1:1:3. TLCP exhibited nematic liquid crystalline mesophase and mai...
Guardado en:
| Autores principales: | , , , |
|---|---|
| Formato: | article |
| Lenguaje: | EN |
| Publicado: |
Nature Portfolio
2021
|
| Materias: | |
| Acceso en línea: | https://doaj.org/article/ccfce65b68474fe9a835bcf1f7420b45 |
| Etiquetas: |
Agregar Etiqueta
Sin Etiquetas, Sea el primero en etiquetar este registro!
|
| Sumario: | Abstract Thermotropic liquid crystal copolyester (TLCP) was synthesized using a melt polymerization method, with a molar ratio composition of 2,5-diethoxy terephthalic acid (ETA), hydroquinone (HQ), and p-hydroxybenzoic acid (HBA) of 1:1:3. TLCP exhibited nematic liquid crystalline mesophase and maintained nematic textures under all heat treatment conditions applied. The synthesized TLCP was processed into fibers using a capillary rheometer. The liquid crystalline mesophase, thermo-mechanical properties, and morphology of TLCP fibers obtained under various heat treatment conditions were investigated. The thermo-mechanical properties of the heat-treated fibers were improved compared to those of the as-spun fibers. The best results were obtained for TLCP fibers annealed at 230 °C for 9 h. The heat-treated fibers showed a well-developed microfiber morphology compared to the as-spun fibers. In the spun fibers, a skin–core morphology was observed regardless of the heat treatment conditions, and a well-developed fiber morphology better than the core area was observed in the skin area. The diameter of the fiber heat-treated at 230 °C for 9 h was approximately 60–110 nm. |
|---|