A Reliable Fracture Angle Determination Algorithm for Extended Puck’s 3D Inter-Fiber Failure Criterion for Unidirectional Composites
Determination of the fracture angle and maximum exposure value of extended Puck’s 3D inter-fiber failure (IFF) criterion is of great importance for predicting the failure mechanism of unidirectional fiber-reinforced composites. In this paper, a reliable semi-analytical algorithm (RSAA) is presented...
Guardado en:
| Autores principales: | , , , , , |
|---|---|
| Formato: | article |
| Lenguaje: | EN |
| Publicado: |
MDPI AG
2021
|
| Materias: | |
| Acceso en línea: | https://doaj.org/article/d49eda408e5b4ba59622d389e07d5e7c |
| Etiquetas: |
Agregar Etiqueta
Sin Etiquetas, Sea el primero en etiquetar este registro!
|
| Sumario: | Determination of the fracture angle and maximum exposure value of extended Puck’s 3D inter-fiber failure (IFF) criterion is of great importance for predicting the failure mechanism of unidirectional fiber-reinforced composites. In this paper, a reliable semi-analytical algorithm (RSAA) is presented for searching fracture angle and corresponding exposure value for the extended Puck’s failure criterion. One hundred million cases are tested for verifying the accuracy of the present and other algorithms on Python using the strength-value-stress-state combinations more universal than those in previous literatures. The reliability of previous algorithms is discussed and counterexamples are provided for illustration. The statistical results show RSAA is adequate for implementation in extended Puck’s criterion and much more reliable than previous algorithms. RSAA can correctly predict the results with a probability of over 99.999%. |
|---|