Bifunctional catalytic effect of Mo2C/oxide interface on multi-layer graphene growth
Abstract The role of the Mo2C/oxide interface on multi-layer graphene (MLG) nucleation during a chemical vapor deposition (CVD) process is investigated. During the CVD process, MLG growth is only observed in the presence of a Mo2C/SiO2 interface, indicating that the chemical reactions occurring at t...
Saved in:
| Main Authors: | , , , , , |
|---|---|
| Format: | article |
| Language: | EN |
| Published: |
Nature Portfolio
2021
|
| Subjects: | |
| Online Access: | https://doaj.org/article/d5a54b7e44944ef6b8e597cf16f121db |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Summary: | Abstract The role of the Mo2C/oxide interface on multi-layer graphene (MLG) nucleation during a chemical vapor deposition (CVD) process is investigated. During the CVD process, MLG growth is only observed in the presence of a Mo2C/SiO2 interface, indicating that the chemical reactions occurring at this interface trigger the nucleation of MLG. The chemical reaction pathway is explained in four steps as (1) creation of H radicals, (2) reduction of the oxide surface, (3) formation of C–C bonds at O–H sites, and (4) expansion of graphitic domains on the Mo2C catalyst. Different Mo2C/oxide interfaces are investigated, with varying affinity for reduction in a hydrogen environment. The results demonstrate a catalyst/oxide bifunctionality on MLG nucleation, comprising of CH4 dehydrogenation by Mo2C and initial C–C bond formation at the oxide interface. |
|---|