Study on cracking cause and rolling process parameters of low carbon steel

When Q215 strip steel is used to coil square tube in iron and steel plant,serious cracking is easy to occur at bending point.In order to reduce the cracking rate of the steel pipe,the causes of the corner cracking of the steel pipe were analyzed from two aspects of the microstructure and the inclusi...

Descripción completa

Guardado en:
Detalles Bibliográficos
Autores principales: Xiaoyong LI, Lei ZHAO, Lin LEI, Yaxu ZHENG, Jie FENG, Zhihong GUO
Formato: article
Lenguaje:ZH
Publicado: Hebei University of Science and Technology 2021
Materias:
T
Acceso en línea:https://doaj.org/article/d6dd2385dd06499b957d95bd52371f61
Etiquetas: Agregar Etiqueta
Sin Etiquetas, Sea el primero en etiquetar este registro!
id oai:doaj.org-article:d6dd2385dd06499b957d95bd52371f61
record_format dspace
spelling oai:doaj.org-article:d6dd2385dd06499b957d95bd52371f612021-11-23T07:08:47ZStudy on cracking cause and rolling process parameters of low carbon steel1008-154210.7535/hbkd.2021yx03011https://doaj.org/article/d6dd2385dd06499b957d95bd52371f612021-06-01T00:00:00Zhttp://xuebao.hebust.edu.cn/hbkjdx/ch/reader/create_pdf.aspx?file_no=b202103011&flag=1&journal_https://doaj.org/toc/1008-1542When Q215 strip steel is used to coil square tube in iron and steel plant,serious cracking is easy to occur at bending point.In order to reduce the cracking rate of the steel pipe,the causes of the corner cracking of the steel pipe were analyzed from two aspects of the microstructure and the inclusions in the steel pipe.The influence mechanism of the microstructure transformation on the cold deformation properties of medium-carbon and low-carbon steel was discussed.The reasonable hot rolling and cooling processes after rolling were formulated.The properties of the inclusions and microstructure in Q215 steel were analyzed by optical microscope and scanning electron microscope.The transformation point,CCT and TTT curves of Q215 steel were calculated by J Mat Pro software.The results show that the main reason for the cracking of the steel pipe is the existence of ter-tiary cementite precipitated along the ferrite grain boundary in the steel,which belongs to hard brittle phase and causes stress concentration at the grain boundary during bending deformation,and the secondary reason for the cracking is the existence of large-size sulfide inclusions more than 100 μm in the steel.By adjusting the hot rolling and cooling process parameters,the amount of tertiary cementite in the steel is significantly reduced,the amount of pearlite is increased,and the cracking rate of the steel pipe is significantly reduced.The research results provide a reference for preventing the processing cracking of Q215 and similar steel grades.Xiaoyong LILei ZHAOLin LEIYaxu ZHENGJie FENGZhihong GUOHebei University of Science and Technologyarticlesteel making; low-carbon steel; steel pipe; cracking; microstructure; inclusion; cementiteTechnologyTZHJournal of Hebei University of Science and Technology, Vol 42, Iss 3, Pp 287-295 (2021)
institution DOAJ
collection DOAJ
language ZH
topic steel making; low-carbon steel; steel pipe; cracking; microstructure; inclusion; cementite
Technology
T
spellingShingle steel making; low-carbon steel; steel pipe; cracking; microstructure; inclusion; cementite
Technology
T
Xiaoyong LI
Lei ZHAO
Lin LEI
Yaxu ZHENG
Jie FENG
Zhihong GUO
Study on cracking cause and rolling process parameters of low carbon steel
description When Q215 strip steel is used to coil square tube in iron and steel plant,serious cracking is easy to occur at bending point.In order to reduce the cracking rate of the steel pipe,the causes of the corner cracking of the steel pipe were analyzed from two aspects of the microstructure and the inclusions in the steel pipe.The influence mechanism of the microstructure transformation on the cold deformation properties of medium-carbon and low-carbon steel was discussed.The reasonable hot rolling and cooling processes after rolling were formulated.The properties of the inclusions and microstructure in Q215 steel were analyzed by optical microscope and scanning electron microscope.The transformation point,CCT and TTT curves of Q215 steel were calculated by J Mat Pro software.The results show that the main reason for the cracking of the steel pipe is the existence of ter-tiary cementite precipitated along the ferrite grain boundary in the steel,which belongs to hard brittle phase and causes stress concentration at the grain boundary during bending deformation,and the secondary reason for the cracking is the existence of large-size sulfide inclusions more than 100 μm in the steel.By adjusting the hot rolling and cooling process parameters,the amount of tertiary cementite in the steel is significantly reduced,the amount of pearlite is increased,and the cracking rate of the steel pipe is significantly reduced.The research results provide a reference for preventing the processing cracking of Q215 and similar steel grades.
format article
author Xiaoyong LI
Lei ZHAO
Lin LEI
Yaxu ZHENG
Jie FENG
Zhihong GUO
author_facet Xiaoyong LI
Lei ZHAO
Lin LEI
Yaxu ZHENG
Jie FENG
Zhihong GUO
author_sort Xiaoyong LI
title Study on cracking cause and rolling process parameters of low carbon steel
title_short Study on cracking cause and rolling process parameters of low carbon steel
title_full Study on cracking cause and rolling process parameters of low carbon steel
title_fullStr Study on cracking cause and rolling process parameters of low carbon steel
title_full_unstemmed Study on cracking cause and rolling process parameters of low carbon steel
title_sort study on cracking cause and rolling process parameters of low carbon steel
publisher Hebei University of Science and Technology
publishDate 2021
url https://doaj.org/article/d6dd2385dd06499b957d95bd52371f61
work_keys_str_mv AT xiaoyongli studyoncrackingcauseandrollingprocessparametersoflowcarbonsteel
AT leizhao studyoncrackingcauseandrollingprocessparametersoflowcarbonsteel
AT linlei studyoncrackingcauseandrollingprocessparametersoflowcarbonsteel
AT yaxuzheng studyoncrackingcauseandrollingprocessparametersoflowcarbonsteel
AT jiefeng studyoncrackingcauseandrollingprocessparametersoflowcarbonsteel
AT zhihongguo studyoncrackingcauseandrollingprocessparametersoflowcarbonsteel
_version_ 1718416913287086080