Mechanical and durability properties of GFRP bars exposed to aggressive solution environments
Two categories of GFRP specimens, in nominal diameters of 11.2 mm and 15.6 mm respectively, made of E-glass fibers and a vinylester resin were immersed in alkaline solution, saline solution and tap water solution at room temperature. The mechanical and durability properties of tested GFRP bar specim...
Guardado en:
Autores principales: | Lu Chunhua, Yang Yuting, He Liyuan |
---|---|
Formato: | article |
Lenguaje: | EN |
Publicado: |
De Gruyter
2021
|
Materias: | |
Acceso en línea: | https://doaj.org/article/d7101c0335744041b2b9abacf718d0e7 |
Etiquetas: |
Agregar Etiqueta
Sin Etiquetas, Sea el primero en etiquetar este registro!
|
Ejemplares similares
-
Effect of Concrete Strength, Arrangement/Ratio of Reinforcement on Flexural Behavior and Cracking of Concrete Beams Reinforced with GFRP Bars
por: Amir Mohammad Mohtaj Khorasani, et al.
Publicado: (2020) -
Effect of bottom ash waste on the rheology and durability of alkali activation pastes
por: Luís U.D. Tambara Júnior, et al.
Publicado: (2022) -
Strength and durability properties of geopolymer paver blocks made with fly ash and brick kiln rice husk ash
por: Shaik Numan Mahdi, et al.
Publicado: (2022) -
Influence of amorphous raw rice husk ash as precursor and curing condition on the performance of alkali activated concrete
por: Thamer Alomayri, et al.
Publicado: (2021) -
On-site corrosion monitoring experience in concrete structures: potential improvements on the current-controlled polarization resistance method
por: J. E. Ramón, et al.
Publicado: (2021)