Volcanic Tuff as Secondary Raw Material in the Production of Clay Bricks
The present work examines an innovative manufacturing technique for fired clay bricks, using tuff as a secondary raw material. Samples were made of clay and tuff (0–30 wt.%) fired at 900 to 1100 °C. The chemical and mineralogical compositions and physical and thermal analyses of raw materials were i...
Guardado en:
| Autores principales: | , , , , , |
|---|---|
| Formato: | article |
| Lenguaje: | EN |
| Publicado: |
MDPI AG
2021
|
| Materias: | |
| Acceso en línea: | https://doaj.org/article/df247d31dc604c33a8dfd328cafe6336 |
| Etiquetas: |
Agregar Etiqueta
Sin Etiquetas, Sea el primero en etiquetar este registro!
|
| Sumario: | The present work examines an innovative manufacturing technique for fired clay bricks, using tuff as a secondary raw material. Samples were made of clay and tuff (0–30 wt.%) fired at 900 to 1100 °C. The chemical and mineralogical compositions and physical and thermal analyses of raw materials were investigated by using SEM-EDS, RX and DTA-TG curves. The samples were analysed from the mineralogical, technological and mechanical points of view. The result show that the tuff’s presence in the clay mixtures considerably reduced the shrinkage of the product during the firing process, and the manufactured samples were of excellent quality. The compressive strength of the bricks varied from 5–35.3MPa, being influenced by the tuff content, clay matrix properties and firing temperatures. Finally, the heat demand for increasing the temperature from room to the firing temperature of the sample with 10% tuff content was 22%. |
|---|