The potential of mesquite (somr) wood in particleboard production

In this study, particleboard was produced using Mesquite (Prosopis juliflora) called Somr wood. Oven dry density of stem and branch wood was measured as 0.92, 0.72 g/cm3 whereas the bark weight percentage of stem and branch wood determined as 13.6 % and14 % respectively. The influence of raw materia...

Descripción completa

Guardado en:

Detalles Bibliográficos
Autores principales:	masoudreza habibi, Hossein Hosseinkhani, Saeed Mahdavi
Formato:	article
Lenguaje:	FA
Publicado:	Regional Information Center for Science and Technology (RICeST) 2012
Materias:	PARTICLEBOARD mesquite wood Resin MOR physical properties Forestry SD1-669.5
Acceso en línea:	https://doaj.org/article/e095a9d8f32d43b78745d955142b3802
Etiquetas:	Agregar Etiqueta Sin Etiquetas, Sea el primero en etiquetar este registro!

id	oai:doaj.org-article:e095a9d8f32d43b78745d955142b3802
record_format	dspace
spelling	oai:doaj.org-article:e095a9d8f32d43b78745d955142b38022021-12-02T03:52:42ZThe potential of mesquite (somr) wood in particleboard production1735-09132383-112X10.22092/ijwpr.2012.117079https://doaj.org/article/e095a9d8f32d43b78745d955142b38022012-03-01T00:00:00Zhttp://ijwpr.areeo.ac.ir/article_117079_5a7e6a60eed21c63f485a9fc761bb232.pdfhttps://doaj.org/toc/1735-0913https://doaj.org/toc/2383-112XIn this study, particleboard was produced using Mesquite (Prosopis juliflora) called Somr wood. Oven dry density of stem and branch wood was measured as 0.92, 0.72 g/cm3 whereas the bark weight percentage of stem and branch wood determined as 13.6 % and14 % respectively. The influence of raw material mixture (stem wood, branch wood, the blend of stem and branch wood, 50/50 w/w) and resin content 10% and 12 % (based on dry weight of the particle) on particleboard properties were investigated. Properties such as MOR, MOE, IB, thickness swelling after 2 and 24 hours immersion in water were determined according to EN standard. Except for MOE, the effect of raw material type on board properties was significant. Particleboards made from branch wood, had the highest MOR. Maximum IB was observed in boards made from the blend of stem and branch wood. With the exception of bending properties, the effect of resin content on all board properties was significant. Increasing the resin content improved board properties. The lowest value of thickness swelling after 2 and 24 hours immersion in water was obtained in particleboard made from stem woodmasoudreza habibiHossein HosseinkhaniSaeed MahdaviRegional Information Center for Science and Technology (RICeST)articlePARTICLEBOARDmesquite woodResinMORphysical propertiesForestrySD1-669.5FAتحقیقات علوم چوب و کاغذ ایران, Vol 27, Iss 1, Pp 51-68 (2012)
institution	DOAJ
collection	DOAJ
language	FA
topic	PARTICLEBOARD mesquite wood Resin MOR physical properties Forestry SD1-669.5
spellingShingle	PARTICLEBOARD mesquite wood Resin MOR physical properties Forestry SD1-669.5 masoudreza habibi Hossein Hosseinkhani Saeed Mahdavi The potential of mesquite (somr) wood in particleboard production
description	In this study, particleboard was produced using Mesquite (Prosopis juliflora) called Somr wood. Oven dry density of stem and branch wood was measured as 0.92, 0.72 g/cm3 whereas the bark weight percentage of stem and branch wood determined as 13.6 % and14 % respectively. The influence of raw material mixture (stem wood, branch wood, the blend of stem and branch wood, 50/50 w/w) and resin content 10% and 12 % (based on dry weight of the particle) on particleboard properties were investigated. Properties such as MOR, MOE, IB, thickness swelling after 2 and 24 hours immersion in water were determined according to EN standard. Except for MOE, the effect of raw material type on board properties was significant. Particleboards made from branch wood, had the highest MOR. Maximum IB was observed in boards made from the blend of stem and branch wood. With the exception of bending properties, the effect of resin content on all board properties was significant. Increasing the resin content improved board properties. The lowest value of thickness swelling after 2 and 24 hours immersion in water was obtained in particleboard made from stem wood
format	article
author	masoudreza habibi Hossein Hosseinkhani Saeed Mahdavi
author_facet	masoudreza habibi Hossein Hosseinkhani Saeed Mahdavi
author_sort	masoudreza habibi
title	The potential of mesquite (somr) wood in particleboard production
title_short	The potential of mesquite (somr) wood in particleboard production
title_full	The potential of mesquite (somr) wood in particleboard production
title_fullStr	The potential of mesquite (somr) wood in particleboard production
title_full_unstemmed	The potential of mesquite (somr) wood in particleboard production
title_sort	potential of mesquite (somr) wood in particleboard production
publisher	Regional Information Center for Science and Technology (RICeST)
publishDate	2012
url	https://doaj.org/article/e095a9d8f32d43b78745d955142b3802
work_keys_str_mv	AT masoudrezahabibi thepotentialofmesquitesomrwoodinparticleboardproduction AT hosseinhosseinkhani thepotentialofmesquitesomrwoodinparticleboardproduction AT saeedmahdavi thepotentialofmesquitesomrwoodinparticleboardproduction AT masoudrezahabibi potentialofmesquitesomrwoodinparticleboardproduction AT hosseinhosseinkhani potentialofmesquitesomrwoodinparticleboardproduction AT saeedmahdavi potentialofmesquitesomrwoodinparticleboardproduction
_version_	1718401584754327552

The potential of mesquite (somr) wood in particleboard production

Ejemplares similares