Influence of V and Zn in FeCrCuMnTi High-Entropy Alloys on Microstructures and Uniaxial Compaction Behavior Prepared by Mechanical Alloying
The densification behavior of FeCrCuMnTi (HEA1), FeCrCuMnTiV (HEA2), and FeCrCuMnTiVZn (HEA3) equiatomic high-entropy alloys (HEAs) was explored using different uniaxial quasi-static controlled compaction (1 mm/min). These HEAs were synthesized by mechanical alloying (MA, speed: 300 rpm, BPR: 10:1,...
Enregistré dans:
Auteurs principaux: | Subbarayan Sivasankaran, Fahad A. Al-Mufadi, Hany R. Ammar |
---|---|
Format: | article |
Langue: | EN |
Publié: |
MDPI AG
2021
|
Sujets: | |
Accès en ligne: | https://doaj.org/article/e16948301a4a42e4b4f3e01c49b394cf |
Tags: |
Ajouter un tag
Pas de tags, Soyez le premier à ajouter un tag!
|
Documents similaires
-
Microstructural Master Alloys Features of Aluminum–Erbium System
par: Sergey Savchenkov, et autres
Publié: (2021) -
Microstructure and Mechanical Properties of Vacuum Diffusion Bonded Zr-4 Alloy Joint
par: Zeming Wang, et autres
Publié: (2021) -
Corrosion Resistance of CoCrFeNiMn High Entropy Alloy Coating Prepared through Plasma Transfer Arc Claddings
par: Pei-Hu Gao, et autres
Publié: (2021) -
The Influence of Ni-Added Fe-Based Pre-Alloy on Microstructure Evolution and Lifetime Extension of Diamond Tools
par: Juan Pu, et autres
Publié: (2021) -
Microstructure and Corrosion Resistance in Bimetal Materials of Q345 and 308 Steel Wire-Arc Additive Manufacturing
par: Qingxian Hu, et autres
Publié: (2021)