Numerical and experimental investigations of built orientation dependent Johnson–Cook model for selective laser melting manufactured AlSi10Mg

Powder bed fusion based additive manufacturing techniques involve melting or sintering of powder particles via laser beams to join them in order to attain desired shapes. This study aims to provide basis for material constitutive parameters of widely used aluminum alloy AlSi10Mg alloy. Initially, te...

Descripción completa

Guardado en:
Detalles Bibliográficos
Autores principales: Murat Aktürk, Mehmet Boy, Munish Kumar Gupta, Saad Waqar, Grzegorz M. Krolczyk, Mehmet Erdi Korkmaz
Formato: article
Lenguaje:EN
Publicado: Elsevier 2021
Materias:
Acceso en línea:https://doaj.org/article/e19579e6737944448ee9f22ad8848f77
Etiquetas: Agregar Etiqueta
Sin Etiquetas, Sea el primero en etiquetar este registro!
Descripción
Sumario:Powder bed fusion based additive manufacturing techniques involve melting or sintering of powder particles via laser beams to join them in order to attain desired shapes. This study aims to provide basis for material constitutive parameters of widely used aluminum alloy AlSi10Mg alloy. Initially, tensile samples of AlSi10Mg alloy samples were manufactured by using SLM technology. Afterwards, through quasi-static and high temperature tensile tests, an attempt has been made to determine the Johnson–Cook material model of AlSi10Mg. in order to conduct quasi-static tensile tests, strain rates of 10−3 s−1, 10−2 s−1 and 5 × 10−2 s−1 were considered and tests were conducted at ambient temperature. Whereas, for high temperature tensile tests 24, 150, 300 °C temperature values were considered at the reference strain rate value of 10−3 s−1. The numerically simulated tensile results achieved by using the established Johnson–Cook model were then compared with experimental results. It was observed that the maximum error between the test and simulation results was around of 7.5%. The error percentage is well within the acceptable, thus proving the accuracy of the established material model.