Reproducibility of small Ge2C6H10O7-added MgB2 bulks fabricated by ex situ Spark Plasma Sintering used in compound bulk magnets with a trapped magnetic field above 5 T
Abstract Bulk discs (20 mm diameter and 4.3 mm thickness) of MgB2 added with Ge2C6H10O7 were obtained by Spark Plasma Sintering. Six samples with composition MgB2(Ge2C6H10O7)0.0014 and one undoped sample were fabricated under similar conditions and were magnetically characterized in order to determi...
Guardado en:
Autores principales: | P. Badica, G. Aldica, M. A. Grigoroscuta, M. Burdusel, I. Pasuk, D. Batalu, K. Berger, A. Koblischka-Veneva, M. R. Koblischka |
---|---|
Formato: | article |
Lenguaje: | EN |
Publicado: |
Nature Portfolio
2020
|
Materias: | |
Acceso en línea: | https://doaj.org/article/e3fc143cedb8427aab9cc9047ff88488 |
Etiquetas: |
Agregar Etiqueta
Sin Etiquetas, Sea el primero en etiquetar este registro!
|
Ejemplares similares
-
On the pinning force in high density MgB2 samples
por: V. Sandu, et al.
Publicado: (2021) -
Antibacterial composite coatings of MgB2 powders embedded in PVP matrix
por: P. Badica, et al.
Publicado: (2021) -
Observation of current-induced bulk magnetization in elemental tellurium
por: Tetsuya Furukawa, et al.
Publicado: (2017) -
Switchable magnetic bulk photovoltaic effect in the two-dimensional magnet CrI3
por: Yang Zhang, et al.
Publicado: (2019) -
Topological phases and bulk-edge correspondence of magnetized cold plasmas
por: Yichen Fu, et al.
Publicado: (2021)