Influence of Feedstock and Final Pyrolysis Temperature on Breaking Strength and Dust Production of Wood-Derived Biochars
The susceptibility to fragmentation of biochar is an important property to consider in field applications. Physical and mechanical properties of wood-derived biochars from vine shoots and holm oak were studied to evaluate the effect of biomass feedstock, final pyrolysis temperature and application c...
Guardado en:
| Autores principales: | , , , , , |
|---|---|
| Formato: | article |
| Lenguaje: | EN |
| Publicado: |
MDPI AG
2021
|
| Materias: | |
| Acceso en línea: | https://doaj.org/article/e56573822dad4782a28da260d1963a2d |
| Etiquetas: |
Agregar Etiqueta
Sin Etiquetas, Sea el primero en etiquetar este registro!
|
| Sumario: | The susceptibility to fragmentation of biochar is an important property to consider in field applications. Physical and mechanical properties of wood-derived biochars from vine shoots and holm oak were studied to evaluate the effect of biomass feedstock, final pyrolysis temperature and application conditions. Vine shoots and holm oak pruning residues were selected for biochar production. Slow pyrolysis experiments were conducted at two different final temperatures (400 and 600 °C). Physical and chemical characteristics of biomass and biochars were determined. Impact strength was evaluated through the measurement of the gravitational potential energy per unit area (J mm<sup>−2</sup>) necessary for the breakage of biochar fragments. Shear strength (N mm<sup>−2</sup>) and a combination of shear/compression strengths (N) were analyzed using a Universal Texture Analyzer. A particular mechanical treatment was carried out on biochar samples to simulate the processing bodies of a commercial manure spreader, under two gravimetric moisture contents. Holm oak-derived biochar was more resistant than vine shoot-derived biochar to the applied forces. Vine shoots-derived biochar did not show a significantly different mechanical behavior between temperatures. Holm Oak-derived biochar produced at the higher final pyrolysis temperature showed higher resistance to be broken into smaller pieces. Moistening resulted in an adequate practice to improve mechanical spreading. |
|---|