Effect of zinc doping on electrical properties of LaAlO3 perovskite
New solid solution with the general formula of LaAl1-xZnxO3-1/2x was prepared by a solid-state reaction route. According to XRD, the crystal structure of LaAlO3 is rhombohedral, while the solid solution possesses cubic symmetry. Homogeneity region of the solid solution LaAl1-xZnxO3-1/2x was narrow a...
Guardado en:
| Autores principales: | , , , , |
|---|---|
| Formato: | article |
| Lenguaje: | EN RU |
| Publicado: |
Uralʹskij federalʹnyj universitet imeni pervogo Prezidenta Rossii B.N. Elʹcina
2021
|
| Materias: | |
| Acceso en línea: | https://doaj.org/article/e8ad8a7bdab146acaff31047d7a71bfd |
| Etiquetas: |
Agregar Etiqueta
Sin Etiquetas, Sea el primero en etiquetar este registro!
|
| Sumario: | New solid solution with the general formula of LaAl1-xZnxO3-1/2x was prepared by a solid-state reaction route. According to XRD, the crystal structure of LaAlO3 is rhombohedral, while the solid solution possesses cubic symmetry. Homogeneity region of the solid solution LaAl1-xZnxO3-1/2x was narrow and limited to the maximum concentration of 5 mol. %. Computer simulations using crystalochemistry and density functional theory approaches showed that LaAlO3 has high energy barriers for O2–-ion transport (2.79 eV). These results are in good agreement with the low values of electrical conductivity obtained experimentally. The electrical conductivity of LaAl1-xZnxO3-1/2x was measured by impedance spectroscopy in the temperature range of 200–1000 °C. The partial substitution of Al3+ by Zn2+ was found to increase the electrical conductivity by ~2 order of magnitude. The electrical conductivity of doped phase LaAl0.95Zn0.05O2.975 as a function of oxygen partial pressure was measured, and the partial contributions (oxygen-ionic and electronic) were determined. It was found that the sample has mixed ionic and p-type electronic conductivity, while the electronic contribution increases with the rise of the temperature. |
|---|