The effect of Bagasse characteristics fibers on MDF properties
In this study, MDF was produced from wet depicting Bagasse in three steaming time of 5, 10 and 15 minutes and in two steaming temperatures of 170°C and 180°C. There were 6 treatment conditions by combination of the above factors and three replications for each combination which resulted in producing...
Guardado en:
| Autores principales: | , , , , , |
|---|---|
| Formato: | article |
| Lenguaje: | FA |
| Publicado: |
Regional Information Center for Science and Technology (RICeST)
2002
|
| Materias: | |
| Acceso en línea: | https://doaj.org/article/ea7da52fdcb2411c8f753a353339a2e3 |
| Etiquetas: |
Agregar Etiqueta
Sin Etiquetas, Sea el primero en etiquetar este registro!
|
| id |
oai:doaj.org-article:ea7da52fdcb2411c8f753a353339a2e3 |
|---|---|
| record_format |
dspace |
| spelling |
oai:doaj.org-article:ea7da52fdcb2411c8f753a353339a2e32021-12-02T02:21:33ZThe effect of Bagasse characteristics fibers on MDF properties1735-09132383-112X10.22092/ijwpr.2002.117514https://doaj.org/article/ea7da52fdcb2411c8f753a353339a2e32002-07-01T00:00:00Zhttp://ijwpr.areeo.ac.ir/article_117514_6c4780d27303c07d2aafabe25ac3ee49.pdfhttps://doaj.org/toc/1735-0913https://doaj.org/toc/2383-112XIn this study, MDF was produced from wet depicting Bagasse in three steaming time of 5, 10 and 15 minutes and in two steaming temperatures of 170°C and 180°C. There were 6 treatment conditions by combination of the above factors and three replications for each combination which resulted in producing 18 boards.The anatomical and chemical properties of Bagasse and also the physical and mechanical properties of MDF such as MOR, MOE, IB and swelling thickness after 2 and 24 hours were studied.Fiber length, fiber diameter, lumen cell diameter, and cell wall thickness were respectively measured 1.24 mm 22.90m., 12.48 m and 5.28m cellulose, lignin, extractives, and ash contents were 53.68%, 20.44%, 0.96% and 1.14% respectively.The measurement of MOR, MOE, IB and SW (after 2 and 24 hours) of the MDF revealed that the proper condition is obtained at the steaming temperature of 170°C and the steaming time of 5 minutes. The properties in the above-mentioned conditions were measured 12.22Mpa, 1370 Mpa, 0.13 Mpa, 47.11% and 52.22% respectively.masoudreza habibiAbdolrahman HosseinzadehFardad GolbabaeiHossein HosseinkhaniJavad SepidedamSaeed MahdaviRegional Information Center for Science and Technology (RICeST)articleMEDIUM DENSITY FIBERBOARDBagasseMECHANICAL PROPERTIESForestrySD1-669.5FAتحقیقات علوم چوب و کاغذ ایران, Vol 7, Iss 16- شماره 293, Pp 29-55 (2002) |
| institution |
DOAJ |
| collection |
DOAJ |
| language |
FA |
| topic |
MEDIUM DENSITY FIBERBOARD Bagasse MECHANICAL PROPERTIES Forestry SD1-669.5 |
| spellingShingle |
MEDIUM DENSITY FIBERBOARD Bagasse MECHANICAL PROPERTIES Forestry SD1-669.5 masoudreza habibi Abdolrahman Hosseinzadeh Fardad Golbabaei Hossein Hosseinkhani Javad Sepidedam Saeed Mahdavi The effect of Bagasse characteristics fibers on MDF properties |
| description |
In this study, MDF was produced from wet depicting Bagasse in three steaming time of 5, 10 and 15 minutes and in two steaming temperatures of 170°C and 180°C. There were 6 treatment conditions by combination of the above factors and three replications for each combination which resulted in producing 18 boards.The anatomical and chemical properties of Bagasse and also the physical and mechanical properties of MDF such as MOR, MOE, IB and swelling thickness after 2 and 24 hours were studied.Fiber length, fiber diameter, lumen cell diameter, and cell wall thickness were respectively measured 1.24 mm 22.90m., 12.48 m and 5.28m cellulose, lignin, extractives, and ash contents were 53.68%, 20.44%, 0.96% and 1.14% respectively.The measurement of MOR, MOE, IB and SW (after 2 and 24 hours) of the MDF revealed that the proper condition is obtained at the steaming temperature of 170°C and the steaming time of 5 minutes. The properties in the above-mentioned conditions were measured 12.22Mpa, 1370 Mpa, 0.13 Mpa, 47.11% and 52.22% respectively. |
| format |
article |
| author |
masoudreza habibi Abdolrahman Hosseinzadeh Fardad Golbabaei Hossein Hosseinkhani Javad Sepidedam Saeed Mahdavi |
| author_facet |
masoudreza habibi Abdolrahman Hosseinzadeh Fardad Golbabaei Hossein Hosseinkhani Javad Sepidedam Saeed Mahdavi |
| author_sort |
masoudreza habibi |
| title |
The effect of Bagasse characteristics fibers on MDF properties |
| title_short |
The effect of Bagasse characteristics fibers on MDF properties |
| title_full |
The effect of Bagasse characteristics fibers on MDF properties |
| title_fullStr |
The effect of Bagasse characteristics fibers on MDF properties |
| title_full_unstemmed |
The effect of Bagasse characteristics fibers on MDF properties |
| title_sort |
effect of bagasse characteristics fibers on mdf properties |
| publisher |
Regional Information Center for Science and Technology (RICeST) |
| publishDate |
2002 |
| url |
https://doaj.org/article/ea7da52fdcb2411c8f753a353339a2e3 |
| work_keys_str_mv |
AT masoudrezahabibi theeffectofbagassecharacteristicsfibersonmdfproperties AT abdolrahmanhosseinzadeh theeffectofbagassecharacteristicsfibersonmdfproperties AT fardadgolbabaei theeffectofbagassecharacteristicsfibersonmdfproperties AT hosseinhosseinkhani theeffectofbagassecharacteristicsfibersonmdfproperties AT javadsepidedam theeffectofbagassecharacteristicsfibersonmdfproperties AT saeedmahdavi theeffectofbagassecharacteristicsfibersonmdfproperties AT masoudrezahabibi effectofbagassecharacteristicsfibersonmdfproperties AT abdolrahmanhosseinzadeh effectofbagassecharacteristicsfibersonmdfproperties AT fardadgolbabaei effectofbagassecharacteristicsfibersonmdfproperties AT hosseinhosseinkhani effectofbagassecharacteristicsfibersonmdfproperties AT javadsepidedam effectofbagassecharacteristicsfibersonmdfproperties AT saeedmahdavi effectofbagassecharacteristicsfibersonmdfproperties |
| _version_ |
1718402563299082240 |