Strain rate sensitivity and mechanical anisotropy of selective laser melted 17-4 PH stainless steel
Quasi-static and dynamic tensile testing was performed upon machined tensile specimens fabricated from bulk primitives produced by the consolidation of water atomized, 17-4 precipitation hardened stainless steel powder by layer-based, selective laser melting. Such mechanical evaluation was performed...
Guardado en:
Autores principales: | , , , |
---|---|
Formato: | article |
Lenguaje: | EN |
Publicado: |
The Japan Society of Mechanical Engineers
2014
|
Materias: | |
Acceso en línea: | https://doaj.org/article/f62661f7e00d418da78c28710a5d279c |
Etiquetas: |
Agregar Etiqueta
Sin Etiquetas, Sea el primero en etiquetar este registro!
|
id |
oai:doaj.org-article:f62661f7e00d418da78c28710a5d279c |
---|---|
record_format |
dspace |
spelling |
oai:doaj.org-article:f62661f7e00d418da78c28710a5d279c2021-11-26T06:12:42ZStrain rate sensitivity and mechanical anisotropy of selective laser melted 17-4 PH stainless steel2187-974510.1299/mej.2014smm0049https://doaj.org/article/f62661f7e00d418da78c28710a5d279c2014-10-01T00:00:00Zhttps://www.jstage.jst.go.jp/article/mej/1/5/1_2014smm0049/_pdf/-char/enhttps://doaj.org/toc/2187-9745Quasi-static and dynamic tensile testing was performed upon machined tensile specimens fabricated from bulk primitives produced by the consolidation of water atomized, 17-4 precipitation hardened stainless steel powder by layer-based, selective laser melting. Such mechanical evaluation was performed by a screw-driven uniaxial tension testing machine and a split-Hopkinson tensile bar apparatus. Strain rates evaluated include 10-3, 10-1 and 103 s-1. Prior to tensile testing, specimens underwent additional thermal processing in accordance with industry standards. Evaluations of the solution heat treatment and peak-age conditions were made alongside similarly prepared, but traditionally processed specimens meeting the same material standard for chemistry (drawn rod). Tensile strength across all strain rates is higher for these selective laser melted (SLM) specimens as a result of microstructure refinement through rapid melt, solidification and cooling during processing. Ultimate tensile and yield strengths increase with increasing strain rate and show no preferential direction relative to the building direction. Elongation anisotropy is observed as a consequence of directional porosity stemming from pores limited to within individual layers. Specimens loaded normal to the SLM building plane commonly rupture at small elongation because of this mechanical fibering from the selective laser melting process.Tyler LEBRUNKenichi TANIGAKIKeitaro HORIKAWAHidetoshi KOBAYASHIThe Japan Society of Mechanical Engineersarticleadditive manufacturingselective laser meltingsplit-hopkinson bar17-4 phstainless steelMechanical engineering and machineryTJ1-1570ENMechanical Engineering Journal, Vol 1, Iss 5, Pp SMM0049-SMM0049 (2014) |
institution |
DOAJ |
collection |
DOAJ |
language |
EN |
topic |
additive manufacturing selective laser melting split-hopkinson bar 17-4 ph stainless steel Mechanical engineering and machinery TJ1-1570 |
spellingShingle |
additive manufacturing selective laser melting split-hopkinson bar 17-4 ph stainless steel Mechanical engineering and machinery TJ1-1570 Tyler LEBRUN Kenichi TANIGAKI Keitaro HORIKAWA Hidetoshi KOBAYASHI Strain rate sensitivity and mechanical anisotropy of selective laser melted 17-4 PH stainless steel |
description |
Quasi-static and dynamic tensile testing was performed upon machined tensile specimens fabricated from bulk primitives produced by the consolidation of water atomized, 17-4 precipitation hardened stainless steel powder by layer-based, selective laser melting. Such mechanical evaluation was performed by a screw-driven uniaxial tension testing machine and a split-Hopkinson tensile bar apparatus. Strain rates evaluated include 10-3, 10-1 and 103 s-1. Prior to tensile testing, specimens underwent additional thermal processing in accordance with industry standards. Evaluations of the solution heat treatment and peak-age conditions were made alongside similarly prepared, but traditionally processed specimens meeting the same material standard for chemistry (drawn rod). Tensile strength across all strain rates is higher for these selective laser melted (SLM) specimens as a result of microstructure refinement through rapid melt, solidification and cooling during processing. Ultimate tensile and yield strengths increase with increasing strain rate and show no preferential direction relative to the building direction. Elongation anisotropy is observed as a consequence of directional porosity stemming from pores limited to within individual layers. Specimens loaded normal to the SLM building plane commonly rupture at small elongation because of this mechanical fibering from the selective laser melting process. |
format |
article |
author |
Tyler LEBRUN Kenichi TANIGAKI Keitaro HORIKAWA Hidetoshi KOBAYASHI |
author_facet |
Tyler LEBRUN Kenichi TANIGAKI Keitaro HORIKAWA Hidetoshi KOBAYASHI |
author_sort |
Tyler LEBRUN |
title |
Strain rate sensitivity and mechanical anisotropy of selective laser melted 17-4 PH stainless steel |
title_short |
Strain rate sensitivity and mechanical anisotropy of selective laser melted 17-4 PH stainless steel |
title_full |
Strain rate sensitivity and mechanical anisotropy of selective laser melted 17-4 PH stainless steel |
title_fullStr |
Strain rate sensitivity and mechanical anisotropy of selective laser melted 17-4 PH stainless steel |
title_full_unstemmed |
Strain rate sensitivity and mechanical anisotropy of selective laser melted 17-4 PH stainless steel |
title_sort |
strain rate sensitivity and mechanical anisotropy of selective laser melted 17-4 ph stainless steel |
publisher |
The Japan Society of Mechanical Engineers |
publishDate |
2014 |
url |
https://doaj.org/article/f62661f7e00d418da78c28710a5d279c |
work_keys_str_mv |
AT tylerlebrun strainratesensitivityandmechanicalanisotropyofselectivelasermelted174phstainlesssteel AT kenichitanigaki strainratesensitivityandmechanicalanisotropyofselectivelasermelted174phstainlesssteel AT keitarohorikawa strainratesensitivityandmechanicalanisotropyofselectivelasermelted174phstainlesssteel AT hidetoshikobayashi strainratesensitivityandmechanicalanisotropyofselectivelasermelted174phstainlesssteel |
_version_ |
1718409818378600448 |