Facile synthesis of highly active Ti/Sb-SnO2 electrode by sol-gel spinning technique for landfill leachate treatment
Highly active Ti/Sb–SnO2 electrodes were fabricated using sol-gel spin coating procedure, which exhibited a rough, uniform and multilayer coating structure. The effects of different Sb-SnO2 film layers on the physiochemical, electrochemical properties and pollutant degradability of electrodes and th...
Guardado en:
| Autores principales: | , , , , , |
|---|---|
| Formato: | article |
| Lenguaje: | EN |
| Publicado: |
IWA Publishing
2021
|
| Materias: | |
| Acceso en línea: | https://doaj.org/article/f980df5bd9f14c93bffffb3dc4688e54 |
| Etiquetas: |
Agregar Etiqueta
Sin Etiquetas, Sea el primero en etiquetar este registro!
|
| Sumario: | Highly active Ti/Sb–SnO2 electrodes were fabricated using sol-gel spin coating procedure, which exhibited a rough, uniform and multilayer coating structure. The effects of different Sb-SnO2 film layers on the physiochemical, electrochemical properties and pollutant degradability of electrodes and the mechanism were evaluated on a systematic basis. The electrodes with more active layers exhibited higher electro-catalytic performance. Upon exceeding 8 layers, the promotion effect of the coating was reduced. Considering various factors, this paper recommends preparing Ti/Sb–SnO2 electrodes coated with 8 layers to obtain higher electro-catalytic ability in landfill leachate treatment. The specific number of coating layers should be determined according to the electrode requirements. This work provided a theoretical basis and technical support for the preparation of Ti-SnO2 electrodes with high electro-catalytic activity and stability, while it still remains a great challenge to achieve an excellent balance between performance and stability before Ti/Sb-SnO2 electrodes can be implemented on a large scale in wastewater treatment. HIGHLIGHTS
Sol-gel spin coating method could be used to exhibit a multilayer coating structure.;
Electrodes with more active layers had higher electro-catalytic performance.;
Upon exceeding 8 layers, the promotion effect of the coating was reduced.;
Ti/Sb-SnO2 electrodes coated with 8 layers could obtain higher electro-catalytic ability during leachate treatment.; |
|---|