Investigating on the possibility of making particleboard from lignocellulosic sources on southern of Iran (Potential for using wood tamarix in particleboard industries).
The physical and mechanical properties were determined of particleboards produced from Tamarix wood using 3 resin contents (9, 10 and 11%) and 3 pressing times (5, 6 and 7 min). Other factors such as resin type, hardener type, closing press time, mat moisture and board density (etc.) were assumed in...
Guardado en:
| Autores principales: | , , , , |
|---|---|
| Formato: | article |
| Lenguaje: | FA |
| Publicado: |
Regional Information Center for Science and Technology (RICeST)
1998
|
| Materias: | |
| Acceso en línea: | https://doaj.org/article/f9e86c09aa434ad68ffc2b10a0241f75 |
| Etiquetas: |
Agregar Etiqueta
Sin Etiquetas, Sea el primero en etiquetar este registro!
|
| Sumario: | The physical and mechanical properties were determined of particleboards produced from Tamarix wood using 3 resin contents (9, 10 and 11%) and 3 pressing times (5, 6 and 7 min). Other factors such as resin type, hardener type, closing press time, mat moisture and board density (etc.) were assumed invariable. Three boards were. produced for each combination of the 2 variable types. Based on DIN-68763 standard physical and mechanical properties including modulus of rupture (MOR), modulus of elasticity (MOE), internal bond (IB) strength and thickness swelling after 2 and 24 h immersion in water (TS2 and TS24) were tested. The best results were obtained with 11% resin and 6 min pressing time. |
|---|