Shot peening increases resistance to cyclic fatigue fracture of endodontic files
Abstract The objective of this study was to assess the resistance to fatigue fracture of conventional nickel–titanium files after undergoing shot peening. Forty NITIFLEX endodontic files, number 30, were divided into two groups; one was submitted to shot peening treatment and the other was not. All...
Guardado en:
Autores principales: | Javier Nino-Barrera, Jose Sanchez-Aleman, Manuel Acosta-Humanez, Luis Gamboa-Martinez, Carlos Cortes-Rodriguez |
---|---|
Formato: | article |
Lenguaje: | EN |
Publicado: |
Nature Portfolio
2021
|
Materias: | |
Acceso en línea: | https://doaj.org/article/fc3d3a89f58d4a2e9bd26a7fa2bf4a63 |
Etiquetas: |
Agregar Etiqueta
Sin Etiquetas, Sea el primero en etiquetar este registro!
|
Ejemplares similares
-
Effect of Shot Peening on Fatigue Properties for Corroded and Uncorroded (CK35) Steel
por: Marwan N. Arbilei, et al.
Publicado: (2019) -
Interaction of Corrosion-Cumulative Fatigue and Shot Peening of 1100-H12 Aluminum Alloy
por: Alalkawi H.J.M, et al.
Publicado: (2015) -
Effect of optimal shot peening time on fatigue life for aluminum alloy 6061-T651
por: Ahmed N. Al-Khazraji
Publicado: (2019) -
Analysis of the Effects of Aggressive Shot Peening on Fatigue Life of 7075 T6 Aluminum Alloy
por: Khairallah S. Jabur
Publicado: (2012) -
Analysis of the Effects of Aggressive Shot Peening on Fatigue Life of 7075 – T6 Aluminum Alloy
por: Khairallah S. Jabur
Publicado: (2012)