SYNTHESIS AND CHARACTERIZATION OF Co-Ni COLLOIDS PREPARED IN NONAQUEOUS SOLVENTS

The synthesis of Co-Ni bimetallic colloids nanoparticles by the CLD method were obtained. The metals were melted and evaporated in a metal atom reactor and cocondensed with ethanol, 2-propanol and 2-methoxyethanol at 77 K. The colloids were characterized by transmission electron microscopy (TEM), ul...

Descripción completa

Guardado en:
Detalles Bibliográficos
Autores principales: CÁRDENAS TRIVIÑO,GALO, LILLO GARRIDO,VIVIANA
Lenguaje:English
Publicado: Sociedad Chilena de Química 2007
Materias:
Acceso en línea:http://www.scielo.cl/scielo.php?script=sci_arttext&pid=S0717-97072007000200014
Etiquetas: Agregar Etiqueta
Sin Etiquetas, Sea el primero en etiquetar este registro!
id oai:scielo:S0717-97072007000200014
record_format dspace
spelling oai:scielo:S0717-970720070002000142007-09-13SYNTHESIS AND CHARACTERIZATION OF Co-Ni COLLOIDS PREPARED IN NONAQUEOUS SOLVENTSCÁRDENAS TRIVIÑO,GALOLILLO GARRIDO,VIVIANA Nano particles colloids cobalt nickel The synthesis of Co-Ni bimetallic colloids nanoparticles by the CLD method were obtained. The metals were melted and evaporated in a metal atom reactor and cocondensed with ethanol, 2-propanol and 2-methoxyethanol at 77 K. The colloids were characterized by transmission electron microscopy (TEM), ultraviolet spectroscopy (UV-VIS), EDX and electrophoresis. The stability at room temperature was also measured. The higher stability dispersion (> 40 days) was Co-Ni/ ethanol, Co-Ni/ 2-methoxyethanol and Co-Ni/ 2-propanol (< 10 days). The electrophoresis showed that particles are positively charged for the alcohols (62 mV for ethanol and 1.4x10-3 mV for 2-propanol) and 9.64 mV negatively charged for 2-methoxyethanol. The particles size of the bimetal colloids ranges from 5.7 to 9.8 nm. The active solids were obtained by solvent evaporation from the colloids dispersion. The microanalysis showed the presence of C, H between 5 to 13% which is indicative that the solvent is incorporated in the solid. The thermogravimetric analysis (TGA) reveals the thermal stability of the active solids. The Co-Ni/ ethanol and Co-Ni/ 2-propanol exhibit a weight loss of 20% w/w, while the Co-Ni/ 2- methoxyethanol shows a weight loss of 42% being the less stable solid. The FTIR of the active solids in KBr pellets exhibit the presence of the solvents incorporated in the active solidinfo:eu-repo/semantics/openAccessSociedad Chilena de QuímicaJournal of the Chilean Chemical Society v.52 n.2 20072007-06-01text/htmlhttp://www.scielo.cl/scielo.php?script=sci_arttext&pid=S0717-97072007000200014en10.4067/S0717-97072007000200014
institution Scielo Chile
collection Scielo Chile
language English
topic Nano particles
colloids
cobalt
nickel
spellingShingle Nano particles
colloids
cobalt
nickel
CÁRDENAS TRIVIÑO,GALO
LILLO GARRIDO,VIVIANA
SYNTHESIS AND CHARACTERIZATION OF Co-Ni COLLOIDS PREPARED IN NONAQUEOUS SOLVENTS
description The synthesis of Co-Ni bimetallic colloids nanoparticles by the CLD method were obtained. The metals were melted and evaporated in a metal atom reactor and cocondensed with ethanol, 2-propanol and 2-methoxyethanol at 77 K. The colloids were characterized by transmission electron microscopy (TEM), ultraviolet spectroscopy (UV-VIS), EDX and electrophoresis. The stability at room temperature was also measured. The higher stability dispersion (> 40 days) was Co-Ni/ ethanol, Co-Ni/ 2-methoxyethanol and Co-Ni/ 2-propanol (< 10 days). The electrophoresis showed that particles are positively charged for the alcohols (62 mV for ethanol and 1.4x10-3 mV for 2-propanol) and 9.64 mV negatively charged for 2-methoxyethanol. The particles size of the bimetal colloids ranges from 5.7 to 9.8 nm. The active solids were obtained by solvent evaporation from the colloids dispersion. The microanalysis showed the presence of C, H between 5 to 13% which is indicative that the solvent is incorporated in the solid. The thermogravimetric analysis (TGA) reveals the thermal stability of the active solids. The Co-Ni/ ethanol and Co-Ni/ 2-propanol exhibit a weight loss of 20% w/w, while the Co-Ni/ 2- methoxyethanol shows a weight loss of 42% being the less stable solid. The FTIR of the active solids in KBr pellets exhibit the presence of the solvents incorporated in the active solid
author CÁRDENAS TRIVIÑO,GALO
LILLO GARRIDO,VIVIANA
author_facet CÁRDENAS TRIVIÑO,GALO
LILLO GARRIDO,VIVIANA
author_sort CÁRDENAS TRIVIÑO,GALO
title SYNTHESIS AND CHARACTERIZATION OF Co-Ni COLLOIDS PREPARED IN NONAQUEOUS SOLVENTS
title_short SYNTHESIS AND CHARACTERIZATION OF Co-Ni COLLOIDS PREPARED IN NONAQUEOUS SOLVENTS
title_full SYNTHESIS AND CHARACTERIZATION OF Co-Ni COLLOIDS PREPARED IN NONAQUEOUS SOLVENTS
title_fullStr SYNTHESIS AND CHARACTERIZATION OF Co-Ni COLLOIDS PREPARED IN NONAQUEOUS SOLVENTS
title_full_unstemmed SYNTHESIS AND CHARACTERIZATION OF Co-Ni COLLOIDS PREPARED IN NONAQUEOUS SOLVENTS
title_sort synthesis and characterization of co-ni colloids prepared in nonaqueous solvents
publisher Sociedad Chilena de Química
publishDate 2007
url http://www.scielo.cl/scielo.php?script=sci_arttext&pid=S0717-97072007000200014
work_keys_str_mv AT cardenastrivinogalo synthesisandcharacterizationofconicolloidspreparedinnonaqueoussolvents
AT lillogarridoviviana synthesisandcharacterizationofconicolloidspreparedinnonaqueoussolvents
_version_ 1718445373220978688