REACTIVITY STUDIES OF MALEIMIDE EPOXY RESIN WITH LONG CHAINED AMINES
After phenylmaleimido group was successfully incorporated into bisphenol-A type epoxy resins (B-13 ) to result in compound possessing both oxirane ring and maleimide reactive groups. The cured maleimide epoxy samples are obtained by thermally curing of the maleimide epoxy (MIE) compounds with alipha...
Guardado en:
| Autores principales: | , , |
|---|---|
| Lenguaje: | English |
| Publicado: |
Sociedad Chilena de Química
2011
|
| Materias: | |
| Acceso en línea: | http://www.scielo.cl/scielo.php?script=sci_arttext&pid=S0717-97072011000300001 |
| Etiquetas: |
Agregar Etiqueta
Sin Etiquetas, Sea el primero en etiquetar este registro!
|
| Sumario: | After phenylmaleimido group was successfully incorporated into bisphenol-A type epoxy resins (B-13 ) to result in compound possessing both oxirane ring and maleimide reactive groups. The cured maleimide epoxy samples are obtained by thermally curing of the maleimide epoxy (MIE) compounds with aliphatic long chained amines such as Tetraethylenepentamine (TEPA), Bishexamethylenetriamine (BHMT), 2-methyl pentamethylenediamine (2-MPMDA) and 2,2,4-trimethy diamines (2,2,4-TMDA) exhibited excellent thermal stability and good chemical (acid/alkali/solvent) and water absorption resistance. Morphological studies by the SEM technique further confirmed the phase homogeneity net work of the cured systems. |
|---|