MICROW AVE-ASSISTED SYNTHESIS OF LOW-SILICA/ALUMINA-RATIO ZEOLITES FROM GEOTHERMAL SILICA
Zeolites A, X, hydroxysodalite and Iiydroxycancrinite (ZA, ZX, ZS, and ZC, respectively) were obtained using geothermal silica (GS) as a raw material and microwaves (MW) as an energy source. GS is an industrial byproduct from the Cerro Prieto geothermal plant in Baja California, México. It is a pote...
Guardado en:
Autores principales: | , , , , , |
---|---|
Lenguaje: | English |
Publicado: |
Sociedad Chilena de Química
2011
|
Materias: | |
Acceso en línea: | http://www.scielo.cl/scielo.php?script=sci_arttext&pid=S0717-97072011000300007 |
Etiquetas: |
Agregar Etiqueta
Sin Etiquetas, Sea el primero en etiquetar este registro!
|
id |
oai:scielo:S0717-97072011000300007 |
---|---|
record_format |
dspace |
spelling |
oai:scielo:S0717-970720110003000072012-01-11MICROW AVE-ASSISTED SYNTHESIS OF LOW-SILICA/ALUMINA-RATIO ZEOLITES FROM GEOTHERMAL SILICADE LEÓN,BEATRIZGAMERO,PRÓCOROMONTERO-OCAMPO,CECILIAVARGAS,GREGORIOESCALANTE-GARCÍA,J. IVÁNMARTÍNEZ,ARTURO I microwaves geothermal silica zeolite Taguchi orthogonal array Zeolites A, X, hydroxysodalite and Iiydroxycancrinite (ZA, ZX, ZS, and ZC, respectively) were obtained using geothermal silica (GS) as a raw material and microwaves (MW) as an energy source. GS is an industrial byproduct from the Cerro Prieto geothermal plant in Baja California, México. It is a potential raw material for zeolite manufacturing because of its chemical composition and its high reactivity given by its small particle size. First, GS was treated with NaOH to generate zeolite precursors; the resulting products were crystallized by MW using sodium alumínate to adjust the SiO2/Al2O3 ratio in the reaction mixture. An experimental design based on an orthogonal array was employed to study the effects of the main factors involved in the zeolitization process of GS. The obtained yields of zeolites ZC, ZA and ZS were 95, 97, and 76.6% respectively. These zeolites were analyzed using X-ray diffraction (XRD), scanning electron microscopy (SEM), and X-ray fluorescence (XRF), and their calcium binding capacity (CBC) was determined. The obtained results were similar to those of commercial zeolites.info:eu-repo/semantics/openAccessSociedad Chilena de QuímicaJournal of the Chilean Chemical Society v.56 n.3 20112011-01-01text/htmlhttp://www.scielo.cl/scielo.php?script=sci_arttext&pid=S0717-97072011000300007en10.4067/S0717-97072011000300007 |
institution |
Scielo Chile |
collection |
Scielo Chile |
language |
English |
topic |
microwaves geothermal silica zeolite Taguchi orthogonal array |
spellingShingle |
microwaves geothermal silica zeolite Taguchi orthogonal array DE LEÓN,BEATRIZ GAMERO,PRÓCORO MONTERO-OCAMPO,CECILIA VARGAS,GREGORIO ESCALANTE-GARCÍA,J. IVÁN MARTÍNEZ,ARTURO I MICROW AVE-ASSISTED SYNTHESIS OF LOW-SILICA/ALUMINA-RATIO ZEOLITES FROM GEOTHERMAL SILICA |
description |
Zeolites A, X, hydroxysodalite and Iiydroxycancrinite (ZA, ZX, ZS, and ZC, respectively) were obtained using geothermal silica (GS) as a raw material and microwaves (MW) as an energy source. GS is an industrial byproduct from the Cerro Prieto geothermal plant in Baja California, México. It is a potential raw material for zeolite manufacturing because of its chemical composition and its high reactivity given by its small particle size. First, GS was treated with NaOH to generate zeolite precursors; the resulting products were crystallized by MW using sodium alumínate to adjust the SiO2/Al2O3 ratio in the reaction mixture. An experimental design based on an orthogonal array was employed to study the effects of the main factors involved in the zeolitization process of GS. The obtained yields of zeolites ZC, ZA and ZS were 95, 97, and 76.6% respectively. These zeolites were analyzed using X-ray diffraction (XRD), scanning electron microscopy (SEM), and X-ray fluorescence (XRF), and their calcium binding capacity (CBC) was determined. The obtained results were similar to those of commercial zeolites. |
author |
DE LEÓN,BEATRIZ GAMERO,PRÓCORO MONTERO-OCAMPO,CECILIA VARGAS,GREGORIO ESCALANTE-GARCÍA,J. IVÁN MARTÍNEZ,ARTURO I |
author_facet |
DE LEÓN,BEATRIZ GAMERO,PRÓCORO MONTERO-OCAMPO,CECILIA VARGAS,GREGORIO ESCALANTE-GARCÍA,J. IVÁN MARTÍNEZ,ARTURO I |
author_sort |
DE LEÓN,BEATRIZ |
title |
MICROW AVE-ASSISTED SYNTHESIS OF LOW-SILICA/ALUMINA-RATIO ZEOLITES FROM GEOTHERMAL SILICA |
title_short |
MICROW AVE-ASSISTED SYNTHESIS OF LOW-SILICA/ALUMINA-RATIO ZEOLITES FROM GEOTHERMAL SILICA |
title_full |
MICROW AVE-ASSISTED SYNTHESIS OF LOW-SILICA/ALUMINA-RATIO ZEOLITES FROM GEOTHERMAL SILICA |
title_fullStr |
MICROW AVE-ASSISTED SYNTHESIS OF LOW-SILICA/ALUMINA-RATIO ZEOLITES FROM GEOTHERMAL SILICA |
title_full_unstemmed |
MICROW AVE-ASSISTED SYNTHESIS OF LOW-SILICA/ALUMINA-RATIO ZEOLITES FROM GEOTHERMAL SILICA |
title_sort |
microw ave-assisted synthesis of low-silica/alumina-ratio zeolites from geothermal silica |
publisher |
Sociedad Chilena de Química |
publishDate |
2011 |
url |
http://www.scielo.cl/scielo.php?script=sci_arttext&pid=S0717-97072011000300007 |
work_keys_str_mv |
AT deleonbeatriz microwaveassistedsynthesisoflowsilicaaluminaratiozeolitesfromgeothermalsilica AT gameroprocoro microwaveassistedsynthesisoflowsilicaaluminaratiozeolitesfromgeothermalsilica AT monteroocampocecilia microwaveassistedsynthesisoflowsilicaaluminaratiozeolitesfromgeothermalsilica AT vargasgregorio microwaveassistedsynthesisoflowsilicaaluminaratiozeolitesfromgeothermalsilica AT escalantegarciajivan microwaveassistedsynthesisoflowsilicaaluminaratiozeolitesfromgeothermalsilica AT martinezarturoi microwaveassistedsynthesisoflowsilicaaluminaratiozeolitesfromgeothermalsilica |
_version_ |
1718445450034413568 |