CORROSION RESISTANCE OF DECORATIVE CHROMIUM FILMS OBTAINED FROM TRIVALENT CHROMIUM SOLUTIONS
In this work, the resistance to corrosion of chromium films obtained from trivalent chromium solutions of different compositions and the influence of solution compounds on the coatings electrochemical behavior and the microstructure were studied. The chromium coatings were obtained from trivalent so...
Guardado en:
Autores principales: | , , , |
---|---|
Lenguaje: | English |
Publicado: |
Sociedad Chilena de Química
2012
|
Materias: | |
Acceso en línea: | http://www.scielo.cl/scielo.php?script=sci_arttext&pid=S0717-97072012000100005 |
Etiquetas: |
Agregar Etiqueta
Sin Etiquetas, Sea el primero en etiquetar este registro!
|
id |
oai:scielo:S0717-97072012000100005 |
---|---|
record_format |
dspace |
spelling |
oai:scielo:S0717-970720120001000052012-07-19CORROSION RESISTANCE OF DECORATIVE CHROMIUM FILMS OBTAINED FROM TRIVALENT CHROMIUM SOLUTIONSSUAREZ,O.JOLAYA,J. JSUAREZ,M.FRODIL,S.E Trivalent chromium plating microstructure corrosion resistance In this work, the resistance to corrosion of chromium films obtained from trivalent chromium solutions of different compositions and the influence of solution compounds on the coatings electrochemical behavior and the microstructure were studied. The chromium coatings were obtained from trivalent solutions in a chloride-based bath with different complexing agents adding also sodium hypophosphite and aluminum chloride. UV-vis spectroscopy was carried out on all solutions before and after plating to observe changes in the chromium complexes chemical state due to the plating process. Scanning Electron Microscopy (SEM) and Energy Dispersive X-ray (EDX) were performed to examine the coatings surface morphology and composition; respectively. The coulometric method was used for measuring coating thickness. Electrochemical impedance spectroscopy (EIS) was done using 3% NaCl as electrolyte and using a three-electrode cell with a standard calomel electrode (SCE) as reference. Bright chromium films were obtained from all baths however, differences were observed concerning morphology, thickness and corrosion resistance depending on the composition of the forming solution.info:eu-repo/semantics/openAccessSociedad Chilena de QuímicaJournal of the Chilean Chemical Society v.57 n.1 20122012-03-01text/htmlhttp://www.scielo.cl/scielo.php?script=sci_arttext&pid=S0717-97072012000100005en10.4067/S0717-97072012000100005 |
institution |
Scielo Chile |
collection |
Scielo Chile |
language |
English |
topic |
Trivalent chromium plating microstructure corrosion resistance |
spellingShingle |
Trivalent chromium plating microstructure corrosion resistance SUAREZ,O.J OLAYA,J. J SUAREZ,M.F RODIL,S.E CORROSION RESISTANCE OF DECORATIVE CHROMIUM FILMS OBTAINED FROM TRIVALENT CHROMIUM SOLUTIONS |
description |
In this work, the resistance to corrosion of chromium films obtained from trivalent chromium solutions of different compositions and the influence of solution compounds on the coatings electrochemical behavior and the microstructure were studied. The chromium coatings were obtained from trivalent solutions in a chloride-based bath with different complexing agents adding also sodium hypophosphite and aluminum chloride. UV-vis spectroscopy was carried out on all solutions before and after plating to observe changes in the chromium complexes chemical state due to the plating process. Scanning Electron Microscopy (SEM) and Energy Dispersive X-ray (EDX) were performed to examine the coatings surface morphology and composition; respectively. The coulometric method was used for measuring coating thickness. Electrochemical impedance spectroscopy (EIS) was done using 3% NaCl as electrolyte and using a three-electrode cell with a standard calomel electrode (SCE) as reference. Bright chromium films were obtained from all baths however, differences were observed concerning morphology, thickness and corrosion resistance depending on the composition of the forming solution. |
author |
SUAREZ,O.J OLAYA,J. J SUAREZ,M.F RODIL,S.E |
author_facet |
SUAREZ,O.J OLAYA,J. J SUAREZ,M.F RODIL,S.E |
author_sort |
SUAREZ,O.J |
title |
CORROSION RESISTANCE OF DECORATIVE CHROMIUM FILMS OBTAINED FROM TRIVALENT CHROMIUM SOLUTIONS |
title_short |
CORROSION RESISTANCE OF DECORATIVE CHROMIUM FILMS OBTAINED FROM TRIVALENT CHROMIUM SOLUTIONS |
title_full |
CORROSION RESISTANCE OF DECORATIVE CHROMIUM FILMS OBTAINED FROM TRIVALENT CHROMIUM SOLUTIONS |
title_fullStr |
CORROSION RESISTANCE OF DECORATIVE CHROMIUM FILMS OBTAINED FROM TRIVALENT CHROMIUM SOLUTIONS |
title_full_unstemmed |
CORROSION RESISTANCE OF DECORATIVE CHROMIUM FILMS OBTAINED FROM TRIVALENT CHROMIUM SOLUTIONS |
title_sort |
corrosion resistance of decorative chromium films obtained from trivalent chromium solutions |
publisher |
Sociedad Chilena de Química |
publishDate |
2012 |
url |
http://www.scielo.cl/scielo.php?script=sci_arttext&pid=S0717-97072012000100005 |
work_keys_str_mv |
AT suarezoj corrosionresistanceofdecorativechromiumfilmsobtainedfromtrivalentchromiumsolutions AT olayajj corrosionresistanceofdecorativechromiumfilmsobtainedfromtrivalentchromiumsolutions AT suarezmf corrosionresistanceofdecorativechromiumfilmsobtainedfromtrivalentchromiumsolutions AT rodilse corrosionresistanceofdecorativechromiumfilmsobtainedfromtrivalentchromiumsolutions |
_version_ |
1718445459111936000 |