CHITOSAN-COPPER PAINT TYPES AS ANTIFOULING
A prototype of antifouling paints was prepared with a Qs-Cu (I)-Fe (II) complex as a possible replacement for traditional antifouling net paints, which contain a large concentration of copper, finding them in an order of 10-30 % depending on the company, and either in water or solvent based. A Qs-Cu...
Guardado en:
| Autores principales: | , |
|---|---|
| Lenguaje: | English |
| Publicado: |
Sociedad Chilena de Química
2014
|
| Materias: | |
| Acceso en línea: | http://www.scielo.cl/scielo.php?script=sci_arttext&pid=S0717-97072014000200004 |
| Etiquetas: |
Agregar Etiqueta
Sin Etiquetas, Sea el primero en etiquetar este registro!
|
| Sumario: | A prototype of antifouling paints was prepared with a Qs-Cu (I)-Fe (II) complex as a possible replacement for traditional antifouling net paints, which contain a large concentration of copper, finding them in an order of 10-30 % depending on the company, and either in water or solvent based. A Qs-Cu complex was prepared, with a solution at 3% with acetic acid, and then Fe2O3 was added to the solution. FT IR analysis was carried out, as well as analysis of the TGA at the Qs and the complex with Qs-Cu, and with the solution, three different paints were prepared. Those that varied volume of diethylene glycol added to them. The analysis of the paints was carried out, once the paint was pervaded in a network of polyamide, through SEM with EDX and TEM, which was purchased with the commercial paints, water based and solvent based. One of the objectives is to be able to compare the coverage of the network with the commercial paint, and that of the complex Qs-Cu. The results showed that the best paint obtained was paint #2, found to be similar to that pervaded with water based paint. |
|---|