Study on preparation and properties of phenol-formaldehyde-chinese fir liquefaction copolymer resin
A new zero-waste and zero-pollution composite adhesive labeled Chinese fir-based adhesive for exterior plywood was synthesized by blending alkaline Chinese fir (Cunninghamia lanceolata) liquid with a small amount of phenol-formaldehyde (PF). The free phenol and free formaldehyde content of the Chine...
Guardado en:
| Autores principales: | , , , , , |
|---|---|
| Lenguaje: | English |
| Publicado: |
Universidad del Bío-Bío
2014
|
| Materias: | |
| Acceso en línea: | http://www.scielo.cl/scielo.php?script=sci_arttext&pid=S0718-221X2014000200003 |
| Etiquetas: |
Agregar Etiqueta
Sin Etiquetas, Sea el primero en etiquetar este registro!
|
| Sumario: | A new zero-waste and zero-pollution composite adhesive labeled Chinese fir-based adhesive for exterior plywood was synthesized by blending alkaline Chinese fir (Cunninghamia lanceolata) liquid with a small amount of phenol-formaldehyde (PF). The free phenol and free formaldehyde content of the Chinese fir-based adhesive were sharply decreased compared to normal PF resin by more than 50%. The synthetic adhesive show with excellent water resistance and environmental friendliness, which had a 28h boil-dry-boil wet bonding strength of 1,73MPa according to standard JIS K6806-2003 and a formaldehyde emission of 0,045mg/L according to standard JIS A1460-2003. The structural properties and their thermal properties of cured adhesives were evaluated using Fourier transform infrared (FT-IR) and differential scanning calorimetry (DSC). The FT-IR analysis confirmed the expected chemical structure as the Chinese fir liquid reacted with formaldehyde and phenol which occurred at the wavenumbers of 1733, 1698, 1652cm-1 and 1077, 1048 cm-1. Although the DSC results indicated that the Chinese fir-based adhesive's curing need higher temperature than the control PF resin, the higher curing temperature hardly cripple the availability of Chinese fir-based resin in the plywood production. |
|---|