Comparison between three-point and four-point flexural tests to determine wood strength of Eucalyptus specimens
Abstract: Comparison between flexural wood strength values obtained from three-point and four-point bending tests in wood were only reported in few previous works, but remains unclear. Thus, the aim of this study was to determine the relationship between wood strength (MOR) obtained by 4-point and 3...
Guardado en:
Autores principales: | , |
---|---|
Lenguaje: | English |
Publicado: |
Universidad del Bío-Bío
2018
|
Materias: | |
Acceso en línea: | http://www.scielo.cl/scielo.php?script=sci_arttext&pid=S0718-221X2018000300333 |
Etiquetas: |
Agregar Etiqueta
Sin Etiquetas, Sea el primero en etiquetar este registro!
|
id |
oai:scielo:S0718-221X2018000300333 |
---|---|
record_format |
dspace |
spelling |
oai:scielo:S0718-221X20180003003332018-09-26Comparison between three-point and four-point flexural tests to determine wood strength of Eucalyptus specimensHein,Paulo Ricardo GherardiBrancheriau,Loïc Acoustic vibration density Eucalyptus grandis static bending test stiffness strength Abstract: Comparison between flexural wood strength values obtained from three-point and four-point bending tests in wood were only reported in few previous works, but remains unclear. Thus, the aim of this study was to determine the relationship between wood strength (MOR) obtained by 4-point and 3-point bending tests in Eucalyptus. Two or three specimens were cut from the same scantling (thus considered as twin) and submitted to flexural vibration tests. Then 190 wood specimens were tested by 4-point bending tests and 138 twin specimens were submitted to 3-point bending tests. Wood strength determined from 3-point bending test presented significantly higher mean value (76,8 MPa) than that from 4-point bending test (73 MPa). A linear regression for converting MOR from 3-point to 4-point bending test was proposed for these Eucalyptus specimens: MOR4p = 0,889 × MOR3p + 5,14 in MPa (R²=0,74). The correlation of MOR in 3-point bending with density was higher (R²=0,57) than in 4-point bending (R²=0,45). The correlations between dynamic elastic moduli and moduli of rupture were similar (circa R²=0,57 for MOR3p and R²=0,65 for MOR4p).info:eu-repo/semantics/openAccessUniversidad del Bío-BíoMaderas. Ciencia y tecnología v.20 n.3 20182018-07-01text/htmlhttp://www.scielo.cl/scielo.php?script=sci_arttext&pid=S0718-221X2018000300333en10.4067/S0718-221X2018005003401 |
institution |
Scielo Chile |
collection |
Scielo Chile |
language |
English |
topic |
Acoustic vibration density Eucalyptus grandis static bending test stiffness strength |
spellingShingle |
Acoustic vibration density Eucalyptus grandis static bending test stiffness strength Hein,Paulo Ricardo Gherardi Brancheriau,Loïc Comparison between three-point and four-point flexural tests to determine wood strength of Eucalyptus specimens |
description |
Abstract: Comparison between flexural wood strength values obtained from three-point and four-point bending tests in wood were only reported in few previous works, but remains unclear. Thus, the aim of this study was to determine the relationship between wood strength (MOR) obtained by 4-point and 3-point bending tests in Eucalyptus. Two or three specimens were cut from the same scantling (thus considered as twin) and submitted to flexural vibration tests. Then 190 wood specimens were tested by 4-point bending tests and 138 twin specimens were submitted to 3-point bending tests. Wood strength determined from 3-point bending test presented significantly higher mean value (76,8 MPa) than that from 4-point bending test (73 MPa). A linear regression for converting MOR from 3-point to 4-point bending test was proposed for these Eucalyptus specimens: MOR4p = 0,889 × MOR3p + 5,14 in MPa (R²=0,74). The correlation of MOR in 3-point bending with density was higher (R²=0,57) than in 4-point bending (R²=0,45). The correlations between dynamic elastic moduli and moduli of rupture were similar (circa R²=0,57 for MOR3p and R²=0,65 for MOR4p). |
author |
Hein,Paulo Ricardo Gherardi Brancheriau,Loïc |
author_facet |
Hein,Paulo Ricardo Gherardi Brancheriau,Loïc |
author_sort |
Hein,Paulo Ricardo Gherardi |
title |
Comparison between three-point and four-point flexural tests to determine wood strength of Eucalyptus specimens |
title_short |
Comparison between three-point and four-point flexural tests to determine wood strength of Eucalyptus specimens |
title_full |
Comparison between three-point and four-point flexural tests to determine wood strength of Eucalyptus specimens |
title_fullStr |
Comparison between three-point and four-point flexural tests to determine wood strength of Eucalyptus specimens |
title_full_unstemmed |
Comparison between three-point and four-point flexural tests to determine wood strength of Eucalyptus specimens |
title_sort |
comparison between three-point and four-point flexural tests to determine wood strength of eucalyptus specimens |
publisher |
Universidad del Bío-Bío |
publishDate |
2018 |
url |
http://www.scielo.cl/scielo.php?script=sci_arttext&pid=S0718-221X2018000300333 |
work_keys_str_mv |
AT heinpauloricardogherardi comparisonbetweenthreepointandfourpointflexuralteststodeterminewoodstrengthofeucalyptusspecimens AT brancheriauloic comparisonbetweenthreepointandfourpointflexuralteststodeterminewoodstrengthofeucalyptusspecimens |
_version_ |
1714202658487664640 |