J e (4.2 K, 31.2 T) beyond 1 kA/mm2 of a ~3.2 μm thick, 20 mol% Zr-added MOCVD REBCO coated conductor
Abstract A main challenge that significantly impedes REBa2Cu3Ox (RE = rare earth) coated conductor applications is the low engineering critical current density J e because of the low superconductor fill factor in a complicated layered structure that is crucial for REBa2Cu3Ox to carry supercurrent. R...
Guardado en:
Autores principales: | A. Xu, Y. Zhang, M. Heydari Gharahcheshmeh, Y. Yao, E. Galstyan, D. Abraimov, F. Kametani, A. Polyanskii, J. Jaroszynski, V. Griffin, G. Majkic, D. C. Larbalestier, V. Selvamanickam |
---|---|
Formato: | article |
Lenguaje: | EN |
Publicado: |
Nature Portfolio
2017
|
Materias: | |
Acceso en línea: | https://doaj.org/article/18724b17806f4b28886612663d4d3f4d |
Etiquetas: |
Agregar Etiqueta
Sin Etiquetas, Sea el primero en etiquetar este registro!
|
Ejemplares similares
-
Effect of heat treatments on superconducting properties and connectivity in K-doped BaFe2As2
por: Chiara Tarantini, et al.
Publicado: (2021) -
Over 15 MA/cm2 of critical current density in 4.8 µm thick, Zr-doped (Gd,Y)Ba2Cu3Ox superconductor at 30 K, 3T
por: Goran Majkic, et al.
Publicado: (2018) -
Prototype REBCO Z1 and Z2 shim coils for ultra high-field
por: Dongkeun Park, et al.
Publicado: (2020) -
Characterization of MOCVD-Prepared CIS Solar Cells
por: Seung Hoon Lee, et al.
Publicado: (2021) -
Climate response to the 8.2 ka event in coastal California
por: Jessica L. Oster, et al.
Publicado: (2017)