Formation, Microstructure, and Conductivity of a Novel Ga2S3-Sb2S3-AgI Chalcogenide System
Abstract Novel glasses in a Ga2S3-Sb2S3-AgI system were prepared with a melt-quenching method, and their glass-forming region was identified. The maximum dissolvable AgI in glasses was 65 mol%. The thermal, optical, and structural properties of glasses were investigated as a function of AgI and Ga2S...
Enregistré dans:
| Auteurs principaux: | , , , , , , , , |
|---|---|
| Format: | article |
| Langue: | EN |
| Publié: |
Nature Portfolio
2018
|
| Sujets: | |
| Accès en ligne: | https://doaj.org/article/3dad931b2ee34b9e83a5064a8fa4f332 |
| Tags: |
Ajouter un tag
Pas de tags, Soyez le premier à ajouter un tag!
|
| Résumé: | Abstract Novel glasses in a Ga2S3-Sb2S3-AgI system were prepared with a melt-quenching method, and their glass-forming region was identified. The maximum dissolvable AgI in glasses was 65 mol%. The thermal, optical, and structural properties of glasses were investigated as a function of AgI and Ga2S3 contents. The Ga2S3-Sb2S3-AgI glasses possess a wide region of transmission window (0.65−14 μm). An ionic conductivity of approximately 1.01 × 10−3 S/cm can be obtained for a 40 (0.8Sb2S3-0.2Ga2S3)-60AgI glass at an ambient temperature, and the ionic conductivity increased as temperature increased. The relative activation energy of Ag+ conduction was also calculated. These novel glasses show potential for the combined application of infrared optics and solid electrolytes. |
|---|