Thermoplastic Intumescent Coatings Modified with Pentaerythritol-Occluded Carbon Nanotubes
A thermoplastic intumescent coating system (IC) based on poly(vinyl acetate) was modified by two forms of multiwalled carbon nanotubes (CNTs), i.e., by a nanofiller powder and its solid dispersions in pentaerythritol (PER-CNTs). It was revealed that only the PER-CNTs modifier allows us to obtain sol...
Saved in:
| Main Authors: | , , , |
|---|---|
| Format: | article |
| Language: | EN |
| Published: |
MDPI AG
2021
|
| Subjects: | |
| Online Access: | https://doaj.org/article/57664bca43ba4e3d9c29e7a8afb2aeb0 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Summary: | A thermoplastic intumescent coating system (IC) based on poly(vinyl acetate) was modified by two forms of multiwalled carbon nanotubes (CNTs), i.e., by a nanofiller powder and its solid dispersions in pentaerythritol (PER-CNTs). It was revealed that only the PER-CNTs modifier allows us to obtain solvent-borne ICs with a relatively high CNTs concentration (1–3 wt. parts of CNTs/100 wt. parts of paint solids) and acceptable application viscosity. Thermal insulation time (TIT) and intumescent factor (<i>IF</i>) of the ICs on a steel substrate (a fire test according to a cellulosic fire curve), as well as morphology, chemical structure (by the FT-IR technique) and mechanical strength of the charred systems, were investigated. It was found that the CNTs powder decreases TIT and <i>IF</i> values while PER-occluded CNTs improve these parameters (e.g., +4.6 min and +102% vs. an unmodified sample, respectively). Compressive strength of the charred ICs was improved by the PER-CNTs modifier as well. |
|---|