Indium-Based Micro-Bump Array Fabrication Technology with Added Pre-Reflow Wet Etching and Annealing
Indium-based micro-bump arrays, among other things, are used for the bonding of infrared photodetectors and focal plane arrays. In this paper, several aspects of the fabrication technology of micrometer-sized indium bumps with a smooth surface morphology were investigated. The thermal evaporation of...
Guardado en:
| Autores principales: | , , , , , , , |
|---|---|
| Formato: | article |
| Lenguaje: | EN |
| Publicado: |
MDPI AG
2021
|
| Materias: | |
| Acceso en línea: | https://doaj.org/article/8dff14f2f68545b7a93c52405de75735 |
| Etiquetas: |
Agregar Etiqueta
Sin Etiquetas, Sea el primero en etiquetar este registro!
|
| Sumario: | Indium-based micro-bump arrays, among other things, are used for the bonding of infrared photodetectors and focal plane arrays. In this paper, several aspects of the fabrication technology of micrometer-sized indium bumps with a smooth surface morphology were investigated. The thermal evaporation of indium has been optimized to achieve ~8 μm-thick layers with a small surface roughness of R<sub>a</sub> = 11 nm, indicating a high packing density of atoms. This ensures bump uniformity across the sample, as well as prevents oxidation inside the In columns prior to the reflow. A series of experiments to optimize indium bump fabrication technology, including a shear test of single columns, is described. A reliable, repeatable, simple, and quick approach was developed with the pre-etching of indium columns in a 10% HCl solution preceded by annealing at 120 °C in N<sub>2</sub>. |
|---|