Modeling porosity loss in Fe0-based permeable reactive barriers with Faraday’s law
Abstract Solid iron corrosion products (FeCPs), continuously generated from iron corrosion in Fe0-based permeable reactive barriers (PRB) at pH > 4.5, can lead to significant porosity loss and possibility of system’s failure. To avoid such failure and to estimate the long-term performance of PRBs...