Influence of V and Zn in FeCrCuMnTi High-Entropy Alloys on Microstructures and Uniaxial Compaction Behavior Prepared by Mechanical Alloying
The densification behavior of FeCrCuMnTi (HEA1), FeCrCuMnTiV (HEA2), and FeCrCuMnTiVZn (HEA3) equiatomic high-entropy alloys (HEAs) was explored using different uniaxial quasi-static controlled compaction (1 mm/min). These HEAs were synthesized by mechanical alloying (MA, speed: 300 rpm, BPR: 10:1,...