Oxygen changes crack modes of Ni-based single crystal superalloy

Oxygen changes crack modes of Ni-based single crystal superalloy

Oxygen-affected cracking commonly presents on thin Ni-based single crystal superalloy components serving in high temperature and oxidizing environments. This study uses a newly developed in-situ thermal-stress environmental transmission electron microscope to investigate the oxidation and fracture b...

Descripción completa

Guardado en:
Detalles Bibliográficos
Autores principales: Xueqiao Li, Yinong Liu, Yunsong Zhao, Yanhui Chen, Ang Li, Jianfei Zhang, Yadi Zhai, Zhipeng Li, Dongfeng Ma, Xiaochen Li, Qing Zhang, Xiaomeng Yang, Haibo Long, Shengcheng Mao, Ze Zhang, Xiaodong Han
Formato: article
Lenguaje:EN
Publicado: Taylor & Francis Group 2021
Materias:
ni-based superalloys
oxidation
environment-assisted cracking
in-situ transmission electron microscopy
Materials of engineering and construction. Mechanics of materials
TA401-492
Acceso en línea:https://doaj.org/article/f9edc0eaf46b44c68e856d679c6764be