Oxygen changes crack modes of Ni-based single crystal superalloy

Oxygen-affected cracking commonly presents on thin Ni-based single crystal superalloy components serving in high temperature and oxidizing environments. This study uses a newly developed in-situ thermal-stress environmental transmission electron microscope to investigate the oxidation and fracture b...

Descripción completa

Guardado en:

Detalles Bibliográficos
Autores principales:	Xueqiao Li, Yinong Liu, Yunsong Zhao, Yanhui Chen, Ang Li, Jianfei Zhang, Yadi Zhai, Zhipeng Li, Dongfeng Ma, Xiaochen Li, Qing Zhang, Xiaomeng Yang, Haibo Long, Shengcheng Mao, Ze Zhang, Xiaodong Han
Formato:	article
Lenguaje:	EN
Publicado:	Taylor & Francis Group 2021
Materias:	ni-based superalloys oxidation environment-assisted cracking in-situ transmission electron microscopy Materials of engineering and construction. Mechanics of materials TA401-492
Acceso en línea:	https://doaj.org/article/f9edc0eaf46b44c68e856d679c6764be
Etiquetas:	Agregar Etiqueta Sin Etiquetas, Sea el primero en etiquetar este registro!

Sea el primero en dejar un comentario!

Oxygen changes crack modes of Ni-based single crystal superalloy

Ejemplares similares