Influence of high-energy ball milling on the optical transmittance and some mechanical and tribological properties of a bone china

Bone china samples were produced using two different milling methods: low-energy ball milling (LEBM) for 3 and 24 h, and high-energy ball milling (HEBM) for 5 min. After pressing, the samples were sintered at temperatures ranging from 1100 °C to 1250 °C. HEBM 5 min yields a raw materials’ specific s...

Descripción completa

Guardado en:

Detalles Bibliográficos
Autores principales:	Victor G. Martins, Carolina Cavion, Júlia Tonet, Luísa de S. Miola, Cláudio A. Perottoni, Janete E. Zorzi
Formato:	article
Lenguaje:	EN ES
Publicado:	Elsevier 2021
Materias:	Porcelana de huesos Molienda de alta energía Transmitancia óptica Propiedades mecánicas Clay industries. Ceramics. Glass TP785-869
Acceso en línea:	https://doaj.org/article/fb71d74016d94f969c2810092205231f
Etiquetas:	Agregar Etiqueta Sin Etiquetas, Sea el primero en etiquetar este registro!

id	oai:doaj.org-article:fb71d74016d94f969c2810092205231f
record_format	dspace
spelling	oai:doaj.org-article:fb71d74016d94f969c2810092205231f2021-11-22T04:17:30ZInfluence of high-energy ball milling on the optical transmittance and some mechanical and tribological properties of a bone china0366-317510.1016/j.bsecv.2020.04.003https://doaj.org/article/fb71d74016d94f969c2810092205231f2021-11-01T00:00:00Zhttp://www.sciencedirect.com/science/article/pii/S0366317520300509https://doaj.org/toc/0366-3175Bone china samples were produced using two different milling methods: low-energy ball milling (LEBM) for 3 and 24 h, and high-energy ball milling (HEBM) for 5 min. After pressing, the samples were sintered at temperatures ranging from 1100 °C to 1250 °C. HEBM 5 min yields a raw materials’ specific surface area (BET) almost 50% higher than LEBM 24 h. The highest density was obtained for samples prepared by HEBM 5 min (2.65 g/cm3), sintered at 1200 °C, which is 4.4% higher than that obtained for the sample made by LEBM 24 h. Samples prepared by HEBM 5 min and LEBM 24 h exhibit similar Vickers hardness, indentation fracture toughness and, wear coefficient. Overall, these samples exhibit better mechanical properties than those of the samples prepared by LEBM 3 h. The milling method influences the translucency of bone china up to a firing temperature of about 1150 °C. Above this temperature, the formation of the liquid phase reduces porosity and, consequently, light scattering, regardless of the milling method used to produce bone china. Even so, HEBM still has a beneficial role in making bone china more homogeneous as compared to those produced by LEBM. Resumen: Las muestras de porcelana de huesos se produjeron utilizando 2 métodos de molienda: baja energía (LEBM) durante 3 y 24 h y alta energía (HEBM) durante 5 min. Después del prensado, las muestras se quemaron entre 1.100 y 1.250 °C. La HEBM 5 min produce una superficie específica de materias primas casi un 50% más alta que la LEBM 24 h. La mayor densidad se obtuvo para muestras preparadas por la HEBM 5 min (2,65 g/cm3) y quemadas a 1.200 °C, el 4,4% más que la obtenida por la LEBM 24 h. Las muestras HEBM 5 min y LEBM 24 h mostraron dureza Vickers, tenacidad a la fractura por indentación y coeficiente de desgaste similares. En general, ambas muestras exhiben mejores propiedades mecánicas que las muestras preparadas por la LEBM 3 h. El método de molienda influye en la translucidez de la porcelana de hueso a una temperatura de cocción de alrededor de 1.150 °C. Por encima de esta temperatura, la formación de la fase líquida reduce la porosidad y la dispersión de la luz, independientemente del método de molienda utilizado para producir porcelana para huesos. Aun así, la HEBM hace que la porcelana de huesos sea más homogénea en comparación con las producidas por la LEBM.Victor G. MartinsCarolina CavionJúlia TonetLuísa de S. MiolaCláudio A. PerottoniJanete E. ZorziElsevierarticlePorcelana de huesosMolienda de alta energíaTransmitancia ópticaPropiedades mecánicasClay industries. Ceramics. GlassTP785-869ENESBoletín de la Sociedad Española de Cerámica y Vidrio, Vol 60, Iss 6, Pp 358-368 (2021)
institution	DOAJ
collection	DOAJ
language	EN ES
topic	Porcelana de huesos Molienda de alta energía Transmitancia óptica Propiedades mecánicas Clay industries. Ceramics. Glass TP785-869
spellingShingle	Porcelana de huesos Molienda de alta energía Transmitancia óptica Propiedades mecánicas Clay industries. Ceramics. Glass TP785-869 Victor G. Martins Carolina Cavion Júlia Tonet Luísa de S. Miola Cláudio A. Perottoni Janete E. Zorzi Influence of high-energy ball milling on the optical transmittance and some mechanical and tribological properties of a bone china
description	Bone china samples were produced using two different milling methods: low-energy ball milling (LEBM) for 3 and 24 h, and high-energy ball milling (HEBM) for 5 min. After pressing, the samples were sintered at temperatures ranging from 1100 °C to 1250 °C. HEBM 5 min yields a raw materials’ specific surface area (BET) almost 50% higher than LEBM 24 h. The highest density was obtained for samples prepared by HEBM 5 min (2.65 g/cm3), sintered at 1200 °C, which is 4.4% higher than that obtained for the sample made by LEBM 24 h. Samples prepared by HEBM 5 min and LEBM 24 h exhibit similar Vickers hardness, indentation fracture toughness and, wear coefficient. Overall, these samples exhibit better mechanical properties than those of the samples prepared by LEBM 3 h. The milling method influences the translucency of bone china up to a firing temperature of about 1150 °C. Above this temperature, the formation of the liquid phase reduces porosity and, consequently, light scattering, regardless of the milling method used to produce bone china. Even so, HEBM still has a beneficial role in making bone china more homogeneous as compared to those produced by LEBM. Resumen: Las muestras de porcelana de huesos se produjeron utilizando 2 métodos de molienda: baja energía (LEBM) durante 3 y 24 h y alta energía (HEBM) durante 5 min. Después del prensado, las muestras se quemaron entre 1.100 y 1.250 °C. La HEBM 5 min produce una superficie específica de materias primas casi un 50% más alta que la LEBM 24 h. La mayor densidad se obtuvo para muestras preparadas por la HEBM 5 min (2,65 g/cm3) y quemadas a 1.200 °C, el 4,4% más que la obtenida por la LEBM 24 h. Las muestras HEBM 5 min y LEBM 24 h mostraron dureza Vickers, tenacidad a la fractura por indentación y coeficiente de desgaste similares. En general, ambas muestras exhiben mejores propiedades mecánicas que las muestras preparadas por la LEBM 3 h. El método de molienda influye en la translucidez de la porcelana de hueso a una temperatura de cocción de alrededor de 1.150 °C. Por encima de esta temperatura, la formación de la fase líquida reduce la porosidad y la dispersión de la luz, independientemente del método de molienda utilizado para producir porcelana para huesos. Aun así, la HEBM hace que la porcelana de huesos sea más homogénea en comparación con las producidas por la LEBM.
format	article
author	Victor G. Martins Carolina Cavion Júlia Tonet Luísa de S. Miola Cláudio A. Perottoni Janete E. Zorzi
author_facet	Victor G. Martins Carolina Cavion Júlia Tonet Luísa de S. Miola Cláudio A. Perottoni Janete E. Zorzi
author_sort	Victor G. Martins
title	Influence of high-energy ball milling on the optical transmittance and some mechanical and tribological properties of a bone china
title_short	Influence of high-energy ball milling on the optical transmittance and some mechanical and tribological properties of a bone china
title_full	Influence of high-energy ball milling on the optical transmittance and some mechanical and tribological properties of a bone china
title_fullStr	Influence of high-energy ball milling on the optical transmittance and some mechanical and tribological properties of a bone china
title_full_unstemmed	Influence of high-energy ball milling on the optical transmittance and some mechanical and tribological properties of a bone china
title_sort	influence of high-energy ball milling on the optical transmittance and some mechanical and tribological properties of a bone china
publisher	Elsevier
publishDate	2021
url	https://doaj.org/article/fb71d74016d94f969c2810092205231f
work_keys_str_mv	AT victorgmartins influenceofhighenergyballmillingontheopticaltransmittanceandsomemechanicalandtribologicalpropertiesofabonechina AT carolinacavion influenceofhighenergyballmillingontheopticaltransmittanceandsomemechanicalandtribologicalpropertiesofabonechina AT juliatonet influenceofhighenergyballmillingontheopticaltransmittanceandsomemechanicalandtribologicalpropertiesofabonechina AT luisadesmiola influenceofhighenergyballmillingontheopticaltransmittanceandsomemechanicalandtribologicalpropertiesofabonechina AT claudioaperottoni influenceofhighenergyballmillingontheopticaltransmittanceandsomemechanicalandtribologicalpropertiesofabonechina AT janeteezorzi influenceofhighenergyballmillingontheopticaltransmittanceandsomemechanicalandtribologicalpropertiesofabonechina
_version_	1718418259290619904

Influence of high-energy ball milling on the optical transmittance and some mechanical and tribological properties of a bone china

Ejemplares similares